Magnesium Alloy ZM10-F vs ZM10-T1
Magnesium Alloy · ZM10 temper comparison
ZM10-F and ZM10-T1 are two conditions of the same magnesium alloy grade, ZM10: F (as fabricated) versus T1 (cooled from hot working and naturally aged). The chemistry is identical, so every difference below comes from the condition. ZM10-T1 is the stronger of the two: yield strength 115 MPa (16.7 ksi) against 95 MPa (13.8 ksi) for ZM10-F, about 21% more; tensile strength follows at 180 MPa (26.1 ksi) vs 165 MPa (23.9 ksi). In exchange, ZM10-F is the more ductile: elongation 2% versus 1.5% for ZM10-T1, and ZM10-T1 is harder (75 HB vs 65 HB).
ZM10-FChoose it when the part is bent, formed or impact-loaded.
ZM10-T1Choose it when strength drives the design.
ZM10-F vs ZM10-T1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Fracture Toughness (K_IC) 11 MPa·√m10 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 1.81 g/cm³0.07 lb/in³ · Melting Point (Solidus) 440°C824 °F · Liquidus Temperature 596°C1,105 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 26 µm/m·K14.4 µin/in·°F · Latent Heat of Fusion 373 J/g160 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -1.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 80 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 330 MJ/kg141,875 BTU/lb · Embodied Carbon (primary production) 30 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZM10-F vs ZM10-T1 — frequently asked
Is ZM10-T1 stronger than ZM10-F?
Yes. ZM10-T1 has a typical yield strength of 115 MPa (16.7 ksi) against 95 MPa (13.8 ksi) for ZM10-F — about 21% more. Tensile strength is 180 MPa (26.1 ksi) vs 165 MPa (23.9 ksi).
Which condition does FabDigit quote by default, F or T1?
T6 is the default ZM10 condition in the FabDigit quote flow (neither F nor T1). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ZM10-F over ZM10-T1?
Pick ZM10-F when the part is bent, formed or impact-loaded. Pick ZM10-T1 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZM10-F and ZM10-T1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.