Magnesium Alloy AM100A-F vs AM100A-T6
Magnesium Alloy · AM100A temper comparison
AM100A-F and AM100A-T6 are two conditions of the same magnesium alloy grade, AM100A: F (as fabricated) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. AM100A-T6 is the stronger of the two: yield strength 152 MPa (22 ksi) against 83 MPa (12 ksi) for AM100A-F, about 83% more; tensile strength follows at 275 MPa (39.9 ksi) vs 150 MPa (21.8 ksi). In exchange, AM100A-F is the more ductile: elongation 2% versus 1% for AM100A-T6, and AM100A-T6 is harder (69 HB vs 53 HB). AM100A-T6 runs hotter in service (120°C vs 110°C continuous). On the shop floor, AM100A-F welds better (very good vs good).
AM100A-FChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
AM100A-T6Choose it when strength drives the design, or when the part sees heat.
AM100A-F vs AM100A-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 45 GPa6.5 Msi · Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Fracture Toughness (K_IC) 12 MPa·√m10.9 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 1.81 g/cm³0.07 lb/in³ · Melting Point (Solidus) 465°C869 °F · Liquidus Temperature 598°C1,108 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 25.2 µm/m·K14 µin/in·°F · Latent Heat of Fusion 373 J/g160 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 12 % IACS · Electrical Resistivity 1.4×10⁻⁷ Ω·m5.51 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -1.55 V · Corrosion Resistance 20 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Same in both: Machinability Rating (AISI 1212 = 100 %) 400% · Formability (cold) 8 / 100 · Castability 82 / 100 · Brazeability / Solderability 20 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 320 MJ/kg137,575 BTU/lb · Embodied Carbon (primary production) 30 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AM100A-F vs AM100A-T6 — frequently asked
Is AM100A-T6 stronger than AM100A-F?
Yes. AM100A-T6 has a typical yield strength of 152 MPa (22 ksi) against 83 MPa (12 ksi) for AM100A-F — about 83% more. Tensile strength is 275 MPa (39.9 ksi) vs 150 MPa (21.8 ksi).
Which condition does FabDigit quote by default, F or T6?
T6 is the default AM100A condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, AM100A-F or AM100A-T6?
AM100A-F. Its weldability rates very good (70/100) against good (60/100) for AM100A-T6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AM100A-F and AM100A-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.