Copper Alloy CuNi2SiCr-TB00 vs CuNi2SiCr-TF00
Copper Alloy · CuNi2SiCr temper comparison
CuNi2SiCr-TB00 and CuNi2SiCr-TF00 are two conditions of the same copper alloy grade, CuNi2SiCr: TB00 (solution heat treated) versus TF00 (solution heat treated and precipitation hardened). The chemistry is identical, so every difference below comes from the condition. CuNi2SiCr-TF00 is the stronger of the two: yield strength 530 MPa (76.9 ksi) against 160 MPa (23.2 ksi) for CuNi2SiCr-TB00, about 3.3 times as much; tensile strength follows at 630 MPa (91.4 ksi) vs 350 MPa (50.8 ksi). In exchange, CuNi2SiCr-TB00 is the more ductile: elongation 40% versus 15% for CuNi2SiCr-TF00, and CuNi2SiCr-TF00 is harder (195 HB vs 90 HB). CuNi2SiCr-TF00 runs hotter in service (350°C vs 200°C continuous) and CuNi2SiCr-TF00 conducts heat better (185 W/m·K vs 100 W/m·K). On the shop floor, CuNi2SiCr-TF00 machines more easily (45 vs 35 out of 100).
CuNi2SiCr-TB00Choose it when the part is bent, formed or impact-loaded.
CuNi2SiCr-TF00Choose it when strength drives the design, or when the part sees heat.
CuNi2SiCr-TB00 vs CuNi2SiCr-TF00: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 132 GPa19.1 Msi · Shear Modulus 50 GPa7.3 Msi · Bulk Modulus 138 GPa20 Msi · Poisson's Ratio 0.34 · Reduction in Area 30% · Compressive Strength 520 MPa75.4 ksi · Charpy V-Notch Impact (RT) 25 J18.4 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8.8 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,050°C1,922 °F · Liquidus Temperature 1,090°C1,994 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 50 / 100 · Castability 50 / 100 · Brazeability / Solderability 70 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CuNi2SiCr-TB00 vs CuNi2SiCr-TF00 — frequently asked
Is CuNi2SiCr-TF00 stronger than CuNi2SiCr-TB00?
Yes. CuNi2SiCr-TF00 has a typical yield strength of 530 MPa (76.9 ksi) against 160 MPa (23.2 ksi) for CuNi2SiCr-TB00 — about 3.3 times as much. Tensile strength is 630 MPa (91.4 ksi) vs 350 MPa (50.8 ksi).
Which condition does FabDigit quote by default, TB00 or TF00?
AB+A is the default CuNi2SiCr condition in the FabDigit quote flow (neither TB00 nor TF00). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, CuNi2SiCr-TB00 or CuNi2SiCr-TF00?
CuNi2SiCr-TF00, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for CuNi2SiCr-TB00.
Ready to make it?
Upload a CAD file and FabDigit prices the part in CuNi2SiCr-TB00 and CuNi2SiCr-TF00 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.