Copper Alloy CuAg0.07-H04 vs CuAg0.07-O60
Copper Alloy · CuAg0.07 temper comparison
CuAg0.07-H04 and CuAg0.07-O60 are two conditions of the same copper alloy grade, CuAg0.07: H04 (full hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. CuAg0.07-H04 is the stronger of the two: yield strength 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for CuAg0.07-O60, about 4.4 times as much; tensile strength follows at 350 MPa (50.8 ksi) vs 220 MPa (31.9 ksi). In exchange, CuAg0.07-O60 is the more ductile: elongation 48% versus 9% for CuAg0.07-H04, and CuAg0.07-H04 is harder (100 HB vs 42 HB). CuAg0.07-H04 runs hotter in service (300°C vs 250°C continuous).
CuAg0.07-H04Choose it when strength drives the design, or when the part sees heat.
CuAg0.07-O60Choose it when the part is bent, formed or impact-loaded.
CuAg0.07-H04 vs CuAg0.07-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 120 GPa17.4 Msi · Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Reduction in Area 55% · Charpy V-Notch Impact (RT) 60 J44.3 ft·lbf · Hardness, Rockwell B 45 HRB
Physical
Density and transition temperatures.
Same in both: Density 8.91 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.7 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 25 / 100 · Weldability 45 / 100 · Castability 55 / 100 · Brazeability / Solderability 90 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CuAg0.07-H04 vs CuAg0.07-O60 — frequently asked
Is CuAg0.07-H04 stronger than CuAg0.07-O60?
Yes. CuAg0.07-H04 has a typical yield strength of 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for CuAg0.07-O60 — about 4.4 times as much. Tensile strength is 350 MPa (50.8 ksi) vs 220 MPa (31.9 ksi).
Which condition does FabDigit quote by default, H04 or O60?
H04 is the default CuAg0.07 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose CuAg0.07-H04 over CuAg0.07-O60?
Pick CuAg0.07-H04 when strength drives the design, or when the part sees heat. Pick CuAg0.07-O60 when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in CuAg0.07-H04 and CuAg0.07-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.