Copper Alloy CC760S-GC vs CC760S-GZ
Copper Alloy · CC760S temper comparison
CC760S-GC and CC760S-GZ are two conditions of the same copper alloy grade, CC760S: GC (continuously cast bar/tube) versus GZ (centrifugally cast). The chemistry is identical, so every difference below comes from the condition. CC760S-GC is the stronger of the two: yield strength 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for CC760S-GZ, about 10% more. In exchange, CC760S-GZ is the more ductile: elongation 35% versus 30% for CC760S-GC, and CC760S-GC is harder (26 HRB vs 22 HRB).
CC760S-GCChoose it when strength drives the design.
CC760S-GZChoose it when the part is bent, formed or impact-loaded.
CC760S-GC vs CC760S-GZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 40 GPa5.8 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34 · Fatigue Strength (Endurance Limit) 85 MPa12.3 ksi
Physical
Density and transition temperatures.
Same in both: Density 8.75 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,000°C1,832 °F · Liquidus Temperature 1,025°C1,877 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 155 W/m·K89.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 33 % IACS · Electrical Resistivity 5.2×10⁻⁸ Ω·m2.05 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Castability 70 / 100 · Brazeability / Solderability 92 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CC760S-GC vs CC760S-GZ — frequently asked
Is CC760S-GC stronger than CC760S-GZ?
Yes. CC760S-GC has a typical yield strength of 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for CC760S-GZ — about 10% more. Tensile strength is 270 MPa (39.2 ksi) vs 260 MPa (37.7 ksi).
Which condition does FabDigit quote by default, GC or GZ?
GS is the default CC760S condition in the FabDigit quote flow (neither GC nor GZ). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose CC760S-GC over CC760S-GZ?
Pick CC760S-GC when strength drives the design. Pick CC760S-GZ when the part is bent, formed or impact-loaded.