Copper Alloy C86300 vs CC751S
Copper Alloy · grade comparison
Copper Alloy C86300 and CC751S are both copper alloy grades. C86300 is the stronger of the two: yield strength 470 MPa (68.2 ksi) against 90 MPa (13.1 ksi) for CC751S, about 5.2 times as much; tensile strength follows at 820 MPa (119 ksi) vs 220 MPa (31.9 ksi). C86300 is harder — 225 HB against 55 HB for CC751S — which matters for wear surfaces and threads. C86300 is lighter (7.65 g/cm³ vs 8.5 g/cm³ for CC751S) and C86300 is stiffer (103 GPa vs 90 GPa). On the shop floor, CC751S machines more easily (very good vs poor), C86300 welds better (30 vs 20 out of 100), and CC751S forms better (25 vs 15 out of 100).
C86300Choose it when strength drives the design, or when surface hardness matters.
CC751SChoose it when the part is machined in volume, or when cost is the deciding factor.
C86300 vs CC751S: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elongation at Break 15% · Reduction in Area 18% · Charpy V-Notch Impact (RT) 20 J14.8 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 175 J/g75.2 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C86300 | CC751S |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$$$$ Specialty | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C86300 vs CC751S — frequently asked
Is C86300 stronger than CC751S?
Yes. C86300 has a typical yield strength of 470 MPa (68.2 ksi) against 90 MPa (13.1 ksi) for CC751S — about 5.2 times as much. Tensile strength is 820 MPa (119 ksi) vs 220 MPa (31.9 ksi).
Which is cheaper, C86300 or CC751S?
CC751S is the lower-cost material: it sits in the premium tier ($$$) while C86300 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C86300 or CC751S?
CC751S. Its machinability rates very good (82/100) against poor (25/100) for C86300; for welding the order is C86300 first (poor, 30/100) then CC751S (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C86300 and CC751S side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.