Copper Alloy C84800 vs ZCuPb17Sn4Zn4
Copper Alloy · grade comparison
Copper Alloy C84800 and ZCuPb17Sn4Zn4 are both copper alloy grades. C84800 is the stronger of the two: yield strength 124 MPa (18 ksi) against 80 MPa (11.6 ksi) for ZCuPb17Sn4Zn4, about 55% more; tensile strength follows at 262 MPa (38 ksi) vs 170 MPa (24.7 ksi). C84800 is the more ductile: elongation 35% versus 8% for ZCuPb17Sn4Zn4, and ZCuPb17Sn4Zn4 is harder (60 HB vs 55 HB). C84800 is lighter (8.55 g/cm³ vs 9.2 g/cm³ for ZCuPb17Sn4Zn4) and C84800 is stiffer (86 GPa vs 76 GPa). On the shop floor, C84800 welds better (poor vs not recommended) and ZCuPb17Sn4Zn4 sits in a lower cost tier (high, $$$$) than C84800 (specialty, $$$$$).
C84800Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
ZCuPb17Sn4Zn4Choose it when cost is the deciding factor.
C84800 vs ZCuPb17Sn4Zn4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Reduction in Area
Compressive Strength
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Castability
Brazeability / Solderability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 88 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Water 250 L/kg30 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C84800 | ZCuPb17Sn4Zn4 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C84800 vs ZCuPb17Sn4Zn4 — frequently asked
Is C84800 stronger than ZCuPb17Sn4Zn4?
Yes. C84800 has a typical yield strength of 124 MPa (18 ksi) against 80 MPa (11.6 ksi) for ZCuPb17Sn4Zn4 — about 55% more. Tensile strength is 262 MPa (38 ksi) vs 170 MPa (24.7 ksi).
Which is cheaper, C84800 or ZCuPb17Sn4Zn4?
ZCuPb17Sn4Zn4 is the lower-cost material: it sits in the high tier ($$$$) while C84800 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, C84800 or ZCuPb17Sn4Zn4?
C84800. Its weldability rates poor (20/100) against not recommended (10/100) for ZCuPb17Sn4Zn4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C84800 and ZCuPb17Sn4Zn4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.