Copper Alloy C84800 vs C93600
Copper Alloy · grade comparison
Copper Alloy C84800 and C93600 are both copper alloy grades. C84800 is the stronger of the two: yield strength 124 MPa (18 ksi) against 110 MPa (16 ksi) for C93600, about 13% more; tensile strength follows at 262 MPa (38 ksi) vs 207 MPa (30 ksi). C84800 is the more ductile: elongation 35% versus 15% for C93600, and C93600 is harder (60 HB vs 55 HB). C84800 is lighter (8.55 g/cm³ vs 8.94 g/cm³ for C93600) and C84800 is stiffer (86 GPa vs 76 GPa). On the shop floor, C84800 welds better (poor vs not recommended).
C84800Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C93600Choose it when the part sees heat.
C84800 vs C93600: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Castability
Brazeability / Solderability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C84800 | C93600 |
|---|---|---|
| Default condition | As Cast | As Cast |
| Relative cost | $$$$$ Specialty | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 9 finishes: Chrome Plating, Copper Plating, Electroless Nickel (EN), Electropolishing, Gold Plating, Nickel Plating, Painting, Silver Plating, Tin Plating.
C84800 vs C93600 — frequently asked
Is C84800 stronger than C93600?
Yes. C84800 has a typical yield strength of 124 MPa (18 ksi) against 110 MPa (16 ksi) for C93600 — about 13% more. Tensile strength is 262 MPa (38 ksi) vs 207 MPa (30 ksi).
Which is cheaper, C84800 or C93600?
Both sit in the same relative cost tier ($$$$$, specialty); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, C84800 or C93600?
C84800. Its weldability rates poor (20/100) against not recommended (10/100) for C93600.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C84800 and C93600 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.