Copper Alloy C51000 vs C65100
Copper Alloy · grade comparison
Copper Alloy C51000 and C65100 are both copper alloy grades. C65100 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 140 MPa (20.3 ksi) for C51000, about 171% more; tensile strength follows at 455 MPa (66 ksi) vs 340 MPa (49.3 ksi). In exchange, C51000 is the more ductile: elongation 60% versus 13% for C65100, and C65100 is harder (150 HB vs 80 HB). C65100 is stiffer (117 GPa vs 110 GPa) and C51000 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C65100 welds better (excellent vs fair) and C65100 sits in a lower cost tier (high, $$$$) than C51000 (specialty, $$$$$).
C51000Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C65100Choose it when strength drives the design, or when it will be welded.
C51000 vs C65100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Brazeability / Solderability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 12
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C51000 | C65100 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C51000 vs C65100 — frequently asked
Is C65100 stronger than C51000?
Yes. C65100 has a typical yield strength of 380 MPa (55.1 ksi) against 140 MPa (20.3 ksi) for C51000 — about 171% more. Tensile strength is 455 MPa (66 ksi) vs 340 MPa (49.3 ksi).
Which is cheaper, C51000 or C65100?
C65100 is the lower-cost material: it sits in the high tier ($$$$) while C51000 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C51000 or C65100?
C65100, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for C51000; for welding the order is C65100 first (excellent, 92/100) then C51000 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C51000 and C65100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.