Copper Alloy C44400-H01 vs C44400-H02
Copper Alloy · C44400 temper comparison
C44400-H01 and C44400-H02 are two conditions of the same copper alloy grade, C44400: H01 (quarter hard) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. C44400-H02 is the stronger of the two: yield strength 345 MPa (50 ksi) against 275 MPa (39.9 ksi) for C44400-H01, about 25% more; tensile strength follows at 462 MPa (67 ksi) vs 415 MPa (60.2 ksi). In exchange, C44400-H01 is the more ductile: elongation 40% versus 25% for C44400-H02, and C44400-H02 is harder (115 HB vs 95 HB).
C44400-H01Choose it when the part is bent, formed or impact-loaded.
C44400-H02Choose it when strength drives the design.
C44400-H01 vs C44400-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.53 g/cm³0.31 lb/in³ · Melting Point (Solidus) 900°C1,652 °F · Liquidus Temperature 935°C1,715 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 110 W/m·K63.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.2 µm/m·K11.2 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 25 % IACS · Electrical Resistivity 6.9×10⁻⁸ Ω·m2.72 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 90 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C44400-H01 vs C44400-H02 — frequently asked
Is C44400-H02 stronger than C44400-H01?
Yes. C44400-H02 has a typical yield strength of 345 MPa (50 ksi) against 275 MPa (39.9 ksi) for C44400-H01 — about 25% more. Tensile strength is 462 MPa (67 ksi) vs 415 MPa (60.2 ksi).
Which condition does FabDigit quote by default, H01 or H02?
O61 is the default C44400 condition in the FabDigit quote flow (neither H01 nor H02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C44400-H01 over C44400-H02?
Pick C44400-H01 when the part is bent, formed or impact-loaded. Pick C44400-H02 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C44400-H01 and C44400-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.