Copper Alloy C33000 vs C69710
Copper Alloy · grade comparison
Copper Alloy C33000 and C69710 are both copper alloy grades. C69710 is the stronger of the two: yield strength 215 MPa (31.2 ksi) against 110 MPa (16 ksi) for C33000, about 95% more; tensile strength follows at 450 MPa (65.3 ksi) vs 340 MPa (49.3 ksi). In exchange, C33000 is the more ductile: elongation 55% versus 25% for C69710, and C69710 is harder (120 HB vs 55 HB). C33000 conducts heat better (121 W/m·K vs 30 W/m·K). On the shop floor, C69710 machines more easily (80 vs 70 out of 100), C69710 welds better (fair vs poor), and C69710 sits in a lower cost tier (premium, $$$) than C33000 (high, $$$$).
C33000Choose it when the part is bent, formed or impact-loaded.
C69710Choose it when strength drives the design, or when the part is machined in volume.
C33000 vs C69710: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 39 GPa5.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 20.2 µm/m·K11.2 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 50%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C33000 | C69710 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C33000 vs C69710 — frequently asked
Is C69710 stronger than C33000?
Yes. C69710 has a typical yield strength of 215 MPa (31.2 ksi) against 110 MPa (16 ksi) for C33000 — about 95% more. Tensile strength is 450 MPa (65.3 ksi) vs 340 MPa (49.3 ksi).
Which is cheaper, C33000 or C69710?
C69710 is the lower-cost material: it sits in the premium tier ($$$) while C33000 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C33000 or C69710?
C69710, by a small margin. Both rate very good for machinability — 80/100 against 70/100 for C33000; for welding the order is C69710 first (fair, 35/100) then C33000 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C33000 and C69710 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.