Copper Alloy C26000 vs C69710
Copper Alloy · grade comparison
Copper Alloy C26000 and C69710 are both copper alloy grades. C69710 is the stronger of the two: yield strength 215 MPa (31.2 ksi) against 105 MPa (15.2 ksi) for C26000, about 105% more; tensile strength follows at 450 MPa (65.3 ksi) vs 325 MPa (47.1 ksi). In exchange, C26000 is the more ductile: elongation 62% versus 25% for C69710, and C69710 is harder (120 HB vs 55 HB). C26000 is stiffer (110 GPa vs 103 GPa) and C26000 conducts heat better (121 W/m·K vs 30 W/m·K). On the shop floor, C69710 machines more easily (very good vs poor) and C69710 sits in a lower cost tier (premium, $$$) than C26000 (high, $$$$).
C26000Choose it when the part is bent, formed or impact-loaded.
C69710Choose it when strength drives the design, or when the part is machined in volume.
C26000 vs C69710: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Same in both: Bulk Modulus 115 GPa16.7 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C26000 | C69710 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C26000 vs C69710 — frequently asked
Is C69710 stronger than C26000?
Yes. C69710 has a typical yield strength of 215 MPa (31.2 ksi) against 105 MPa (15.2 ksi) for C26000 — about 105% more. Tensile strength is 450 MPa (65.3 ksi) vs 325 MPa (47.1 ksi).
Which is cheaper, C26000 or C69710?
C69710 is the lower-cost material: it sits in the premium tier ($$$) while C26000 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C26000 or C69710?
C69710. Its machinability rates very good (80/100) against poor (30/100) for C26000; for welding the order is C26000 first (fair, 40/100) then C69710 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C26000 and C69710 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.