Copper Alloy C23000 vs C33000
Copper Alloy · grade comparison
Copper Alloy C23000 and C33000 are both copper alloy grades. C33000 is the stronger of the two: yield strength 110 MPa (16 ksi) against 85 MPa (12.3 ksi) for C23000, about 29% more; tensile strength follows at 340 MPa (49.3 ksi) vs 280 MPa (40.6 ksi). C33000 is the more ductile: elongation 55% versus 45% for C23000, and C33000 is harder (55 HB vs 46 HB). C33000 is lighter (8.47 g/cm³ vs 8.75 g/cm³ for C23000) and C23000 is stiffer (117 GPa vs 103 GPa). On the shop floor, C33000 machines more easily (very good vs poor) and C23000 welds better (good vs poor).
C23000Choose it when it will be welded.
C33000Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C23000 vs C33000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 20
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C23000 | C33000 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | O |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| Chrome Plating | — | Yes |
| Electropolishing | — | Yes |
| Nickel Plating | — | Yes |
| Painting | — | Yes |
| Tin Plating | — | Yes |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C23000 vs C33000 — frequently asked
Is C33000 stronger than C23000?
Yes. C33000 has a typical yield strength of 110 MPa (16 ksi) against 85 MPa (12.3 ksi) for C23000 — about 29% more. Tensile strength is 340 MPa (49.3 ksi) vs 280 MPa (40.6 ksi).
Which is cheaper, C23000 or C33000?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C23000 or C33000?
C33000. Its machinability rates very good (70/100) against poor (28/100) for C23000; for welding the order is C23000 first (good, 55/100) then C33000 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C23000 and C33000 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.