Copper Alloy C19025-H02 vs C19025-O60
Copper Alloy · C19025 temper comparison
C19025-H02 and C19025-O60 are two conditions of the same copper alloy grade, C19025: H02 (half hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C19025-H02 is the stronger of the two: yield strength 430 MPa (62.4 ksi) against 180 MPa (26.1 ksi) for C19025-O60, about 139% more; tensile strength follows at 500 MPa (72.5 ksi) vs 380 MPa (55.1 ksi). In exchange, C19025-O60 is the more ductile: elongation 25% versus 10% for C19025-H02, and C19025-H02 is harder (155 HV vs 110 HV). C19025-O60 runs hotter in service (200°C vs 150°C continuous) and C19025-O60 conducts electricity better (48 % IACS vs 43 % IACS).
C19025-H02Choose it when strength drives the design.
C19025-O60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C19025-H02 vs C19025-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 125 GPa18.1 Msi · Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 135 GPa19.6 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.9 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,070°C1,958 °F · Liquidus Temperature 1,090°C1,994 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.5 µm/m·K9.7 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Brazeability / Solderability 85 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.9 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C19025-H02 vs C19025-O60 — frequently asked
Is C19025-H02 stronger than C19025-O60?
Yes. C19025-H02 has a typical yield strength of 430 MPa (62.4 ksi) against 180 MPa (26.1 ksi) for C19025-O60 — about 139% more. Tensile strength is 500 MPa (72.5 ksi) vs 380 MPa (55.1 ksi).
Which condition does FabDigit quote by default, H02 or O60?
HR04 is the default C19025 condition in the FabDigit quote flow (neither H02 nor O60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C19025-H02 over C19025-O60?
Pick C19025-H02 when strength drives the design. Pick C19025-O60 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C19025-H02 and C19025-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.