Copper Alloy C14500 vs C17465
Copper Alloy · grade comparison
Copper Alloy C14500 and C17465 are both copper alloy grades. C17465 is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 275 MPa (39.9 ksi) for C14500, about 100% more; tensile strength follows at 690 MPa (100 ksi) vs 310 MPa (45 ksi). In exchange, C14500 is the more ductile: elongation 18% versus 15% for C17465, and C17465 is harder (195 HB vs 85 HB). C17465 is stiffer (138 GPa vs 117 GPa) and C17465 runs hotter in service (300°C vs 200°C continuous). On the shop floor, C14500 machines more easily (excellent vs good).
C14500Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
C17465Choose it when strength drives the design, or when the part sees heat.
C14500 vs C17465: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Reduction in Area
Compressive Strength
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Max Service Temperature (continuous)
Same in both: Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Brazeability / Solderability
Machinability Rating (AISI 1212 = 100 %)
Castability
Same in both: Weldability 25 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 260 L/kg31.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C14500 | C17465 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | H02 | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C14500 vs C17465 — frequently asked
Is C17465 stronger than C14500?
Yes. C17465 has a typical yield strength of 550 MPa (79.8 ksi) against 275 MPa (39.9 ksi) for C14500 — about 100% more. Tensile strength is 690 MPa (100 ksi) vs 310 MPa (45 ksi).
Which is cheaper, C14500 or C17465?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C14500 or C17465?
C14500. Its machinability rates excellent (85/100) against good (65/100) for C17465.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C14500 and C17465 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.