Copper Alloy C10200 vs C14500
Copper Alloy · grade comparison
Copper Alloy C10200 and C14500 are both copper alloy grades. C14500 is the stronger of the two: yield strength 275 MPa (39.9 ksi) against 69 MPa (10 ksi) for C10200, about 4.0 times as much; tensile strength follows at 310 MPa (45 ksi) vs 221 MPa (32.1 ksi). In exchange, C10200 is the more ductile: elongation 45% versus 18% for C14500, and C14500 is harder (85 HB vs 45 HB). C10200 runs hotter in service (250°C vs 200°C continuous) and C10200 conducts heat better (391 W/m·K vs 350 W/m·K). On the shop floor, C14500 machines more easily (excellent vs poor) and C10200 welds better (good vs poor).
C10200Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C14500Choose it when strength drives the design, or when the part is machined in volume.
C10200 vs C14500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8.94 g/cm³0.32 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 13.1 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C10200 | C14500 |
|---|---|---|
| Default condition | O | H02 |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 9 finishes: Chrome Plating, Copper Plating, Electroless Nickel (EN), Electropolishing, Gold Plating, Nickel Plating, Painting, Silver Plating, Tin Plating.
C10200 vs C14500 — frequently asked
Is C14500 stronger than C10200?
Yes. C14500 has a typical yield strength of 275 MPa (39.9 ksi) against 69 MPa (10 ksi) for C10200 — about 4.0 times as much. Tensile strength is 310 MPa (45 ksi) vs 221 MPa (32.1 ksi).
Which is cheaper, C10200 or C14500?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C10200 or C14500?
C14500. Its machinability rates excellent (85/100) against poor (22/100) for C10200; for welding the order is C10200 first (good, 65/100) then C14500 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C10200 and C14500 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.