Copper Alloy C10200 vs C11100
Copper Alloy · grade comparison
Copper Alloy C10200 and C11100 are both copper alloy grades. C11100 is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 69 MPa (10 ksi) for C10200, about 4.9 times as much; tensile strength follows at 400 MPa (58 ksi) vs 221 MPa (32.1 ksi). In exchange, C10200 is the more ductile: elongation 45% versus 3% for C11100, and C11100 is harder (100 HB vs 45 HB). On the shop floor, C10200 welds better (good vs poor).
C10200Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C11100Choose it when strength drives the design.
C10200 vs C11100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Max Service Temperature (continuous) 250°C482 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 13.1 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C10200 | C11100 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C10200 vs C11100 — frequently asked
Is C11100 stronger than C10200?
Yes. C11100 has a typical yield strength of 340 MPa (49.3 ksi) against 69 MPa (10 ksi) for C10200 — about 4.9 times as much. Tensile strength is 400 MPa (58 ksi) vs 221 MPa (32.1 ksi).
Which is cheaper, C10200 or C11100?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C10200 or C11100?
C11100, by a small margin. Both rate poor for machinability — 30/100 against 22/100 for C10200; for welding the order is C10200 first (good, 65/100) then C11100 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C10200 and C11100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.