M40J vs T1000G
Composite · grade comparison
M40J and T1000G are both composite grades. T1000G is the stronger of the two: tensile strength 6,370 MPa (924 ksi) against 4,410 MPa (640 ksi) for M40J, about 44% more. T1000G is the more ductile: elongation 2.2% versus 1.2% for M40J. M40J is stiffer (377 GPa vs 294 GPa) and M40J conducts heat better (55 W/m·K vs 10 W/m·K). On the shop floor, M40J machines more easily (25 vs 15 out of 100).
M40JChoose it when the part is machined in volume.
T1000GChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
M40J vs T1000G: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Same in both: Poisson's Ratio 0.27
Physical
Density and transition temperatures.
Density
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 750 J/kg·K0.18 BTU/lb·°F · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | M40J | T1000G |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
M40J vs T1000G — frequently asked
Is T1000G stronger than M40J?
Yes. T1000G has a typical tensile strength of 6,370 MPa (924 ksi) against 4,410 MPa (640 ksi) for M40J — about 44% more.
Which is cheaper, M40J or T1000G?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, M40J or T1000G?
M40J, by a small margin. Both rate poor for machinability — 25/100 against 15/100 for T1000G.
Ready to make it?
Upload a CAD file and FabDigit prices the part in M40J and T1000G side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.