AS4 vs T300
Composite · grade comparison
AS4 and T300 are both composite grades. AS4 is the stronger of the two: tensile strength 4,433 MPa (643 ksi) against 3,530 MPa (512 ksi) for T300, about 26% more. AS4 is the more ductile: elongation 1.8% versus 1.5% for T300. AS4 runs hotter in service (400°C vs 350°C continuous) and T300 conducts heat better (10.5 W/m·K vs 6.8 W/m·K).
AS4Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AS4 vs T300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Physical
Density and transition temperatures.
Density
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Volume Resistivity
Same in both: Electrical Resistivity 1.7×10⁻⁵ Ω·m669 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AS4 | T300 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
AS4 vs T300 — frequently asked
Is AS4 stronger than T300?
Yes. AS4 has a typical tensile strength of 4,433 MPa (643 ksi) against 3,530 MPa (512 ksi) for T300 — about 26% more.
Which is cheaper, AS4 or T300?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, AS4 or T300?
AS4, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for T300.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AS4 and T300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.