6061/SiC/10p vs SCS-6/Ti-6Al-4V
Composite · grade comparison
6061/SiC/10p and SCS-6/Ti-6Al-4V are both composite grades. SCS-6/Ti-6Al-4V is the stronger of the two: yield strength 1,100 MPa (160 ksi) against 296 MPa (42.9 ksi) for 6061/SiC/10p, about 3.7 times as much; tensile strength follows at 1,750 MPa (254 ksi) vs 338 MPa (49 ksi). In exchange, 6061/SiC/10p is the more ductile: elongation 6% versus 0.85% for SCS-6/Ti-6Al-4V. 6061/SiC/10p is lighter (2.75 g/cm³ vs 3.93 g/cm³ for SCS-6/Ti-6Al-4V) and SCS-6/Ti-6Al-4V is stiffer (205 GPa vs 81 GPa). On the shop floor, 6061/SiC/10p machines more easily (poor vs not recommended).
6061/SiC/10pChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
SCS-6/Ti-6Al-4VChoose it when strength drives the design, or when the part sees heat.
6061/SiC/10p vs SCS-6/Ti-6Al-4V: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Physical
Density and transition temperatures.
Density
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Max Service Temperature (short-term)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 6061/SiC/10p | SCS-6/Ti-6Al-4V |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
6061/SiC/10p vs SCS-6/Ti-6Al-4V — frequently asked
Is SCS-6/Ti-6Al-4V stronger than 6061/SiC/10p?
Yes. SCS-6/Ti-6Al-4V has a typical yield strength of 1,100 MPa (160 ksi) against 296 MPa (42.9 ksi) for 6061/SiC/10p — about 3.7 times as much. Tensile strength is 1,750 MPa (254 ksi) vs 338 MPa (49 ksi).
Which is cheaper, 6061/SiC/10p or SCS-6/Ti-6Al-4V?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 6061/SiC/10p or SCS-6/Ti-6Al-4V?
6061/SiC/10p. Its machinability rates poor (30/100) against not recommended (5/100) for SCS-6/Ti-6Al-4V.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6061/SiC/10p and SCS-6/Ti-6Al-4V side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.