TT7K12 vs YG3
Ceramic · grade comparison
TT7K12 and YG3 are both ceramic grades. TT7K12 is the more ductile: elongation 0.2% versus 0% for YG3, and YG3 is harder (1,580 HV vs 1,200 HV). TT7K12 is lighter (13.15 g/cm³ vs 15.1 g/cm³ for YG3) and YG3 is stiffer (650 GPa vs 520 GPa).
TT7K12Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
TT7K12 vs YG3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Same in both: Hardness, Mohs 9
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Volume Resistivity
Same in both: Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | TT7K12 | YG3 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
TT7K12 vs YG3 — frequently asked
What is the difference between TT7K12 and YG3?
TT7K12 and YG3 are both ceramic grades. TT7K12 is the more ductile: elongation 0.2% versus 0% for YG3, and YG3 is harder (1,580 HV vs 1,200 HV). TT7K12 is lighter (13.15 g/cm³ vs 15.1 g/cm³ for YG3) and YG3 is stiffer (650 GPa vs 520 GPa).
Which is cheaper, TT7K12 or YG3?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose TT7K12 over YG3?
Pick TT7K12 when the part is bent, formed or impact-loaded, or when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in TT7K12 and YG3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.