LAS vs Steatite
Ceramic · grade comparison
LAS and Steatite are both ceramic grades. Steatite is the stronger of the two: tensile strength 60 MPa (8.7 ksi) against 45 MPa (6.53 ksi) for LAS, about 33% more. LAS is lighter (2.42 g/cm³ vs 2.8 g/cm³ for Steatite) and Steatite is stiffer (100 GPa vs 72 GPa).
LASChoose it when weight is the constraint, or when the part sees heat.
SteatiteChoose it when strength drives the design.
LAS vs Steatite: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Shear Strength
Hardness, Knoop
Hardness, Mohs
Same in both: Elongation at Break 0% · Fracture Toughness (K_IC) 1.5 MPa·√m1.4 ksi·√in · Hardness, Vickers 650 HV
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Polishability 60 / 100 · Sintering / Firing Temperature 1,300°C2,372 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | LAS | Steatite |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
LAS vs Steatite — frequently asked
Is Steatite stronger than LAS?
Yes. Steatite has a typical tensile strength of 60 MPa (8.7 ksi) against 45 MPa (6.53 ksi) for LAS — about 33% more.
Which is cheaper, LAS or Steatite?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose LAS over Steatite?
Pick LAS when weight is the constraint, or when the part sees heat. Pick Steatite when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in LAS and Steatite side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.