Aluminum AC1B-T6 vs AC1B-T7
Aluminum · AC1B temper comparison
AC1B-T6 and AC1B-T7 are two conditions of the same aluminum grade, AC1B: T6 (solution heat treated and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. AC1B-T6 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for AC1B-T7, about 9% more; tensile strength follows at 350 MPa (50.8 ksi) vs 300 MPa (43.5 ksi). AC1B-T6 is the more ductile: elongation 6% versus 5% for AC1B-T7, and AC1B-T6 is harder (100 HB vs 90 HB). AC1B-T7 runs hotter in service (250°C vs 200°C continuous).
AC1B-T6Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AC1B-T7Choose it when the part sees heat.
AC1B-T6 vs AC1B-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33 · Compressive Strength 260 MPa37.7 ksi · Shear Strength 220 MPa31.9 ksi · Fracture Toughness (K_IC) 24 MPa·√m21.8 ksi·√in · Charpy V-Notch Impact (RT) 8 J5.9 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 545°C1,013 °F · Liquidus Temperature 645°C1,193 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.5 µm/m·K12.5 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.2×10⁻⁸ Ω·m2.05 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.7 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 300% · Weldability 30 / 100 · Castability 40 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AC1B-T6 vs AC1B-T7 — frequently asked
Is AC1B-T6 stronger than AC1B-T7?
Yes. AC1B-T6 has a typical yield strength of 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for AC1B-T7 — about 9% more. Tensile strength is 350 MPa (50.8 ksi) vs 300 MPa (43.5 ksi).
Which condition does FabDigit quote by default, T6 or T7?
T6 is the default AC1B condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose AC1B-T6 over AC1B-T7?
Pick AC1B-T6 when strength drives the design, or when the part is bent, formed or impact-loaded. Pick AC1B-T7 when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AC1B-T6 and AC1B-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.