Aluminum A1N00-H26 vs A1N00-O
Aluminum · A1N00 temper comparison
A1N00-H26 and A1N00-O are two conditions of the same aluminum grade, A1N00: H26 (strain hardened and partially annealed, three-quarter hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. A1N00-H26 is the stronger of the two: yield strength 125 MPa (18.1 ksi) against 35 MPa (5.08 ksi) for A1N00-O, about 3.6 times as much; tensile strength follows at 145 MPa (21 ksi) vs 90 MPa (13.1 ksi). In exchange, A1N00-O is the more ductile: elongation 38% versus 8% for A1N00-H26, and A1N00-H26 is harder (38 HB vs 23 HB). A1N00-O runs hotter in service (200°C vs 130°C continuous). On the shop floor, A1N00-H26 machines more easily (32 vs 22 out of 100).
A1N00-H26Choose it when strength drives the design, or when the part is machined in volume.
A1N00-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A1N00-H26 vs A1N00-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 643°C1,189 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 904 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 72 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 90 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A1N00-H26 vs A1N00-O — frequently asked
Is A1N00-H26 stronger than A1N00-O?
Yes. A1N00-H26 has a typical yield strength of 125 MPa (18.1 ksi) against 35 MPa (5.08 ksi) for A1N00-O — about 3.6 times as much. Tensile strength is 145 MPa (21 ksi) vs 90 MPa (13.1 ksi).
Which condition does FabDigit quote by default, H26 or O?
O is the default A1N00 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A1N00-H26 or A1N00-O?
A1N00-H26, by a small margin. Both rate poor for machinability — 32/100 against 22/100 for A1N00-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A1N00-H26 and A1N00-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.