Aluminum 7017-T651 vs 7017-T7351
Aluminum · 7017 temper comparison
7017-T651 and 7017-T7351 are two conditions of the same aluminum grade, 7017: T651 (T6, stress relieved by stretching) versus T7351 (T73, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 7017-T651 is the stronger of the two: yield strength 390 MPa (56.6 ksi) against 340 MPa (49.3 ksi) for 7017-T7351, about 15% more; tensile strength follows at 455 MPa (66 ksi) vs 412 MPa (59.8 ksi). 7017-T651 is harder — 138 HB against 126 HB for 7017-T7351 — which matters for wear surfaces and threads. 7017-T7351 runs hotter in service (150°C vs 120°C continuous) and 7017-T7351 conducts electricity better (38 % IACS vs 32 % IACS).
7017-T651Choose it when strength drives the design, or when surface hardness matters.
7017-T7351Choose it when the part sees heat.
7017-T651 vs 7017-T7351: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Hardness, Vickers 150 HV
Physical
Density and transition temperatures.
Same in both: Density 2.78 g/cm³0.1 lb/in³ · Melting Point (Solidus) 590°C1,094 °F · Liquidus Temperature 640°C1,184 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 875 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.4×10⁻⁸ Ω·m2.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Same in both: Machinability 68 / 100 · Machinability Rating (AISI 1212 = 100 %) 70% · Weldability 72 / 100 · Castability 30 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
7017-T651 vs 7017-T7351 — frequently asked
Is 7017-T651 stronger than 7017-T7351?
Yes. 7017-T651 has a typical yield strength of 390 MPa (56.6 ksi) against 340 MPa (49.3 ksi) for 7017-T7351 — about 15% more. Tensile strength is 455 MPa (66 ksi) vs 412 MPa (59.8 ksi).
Which condition does FabDigit quote by default, T651 or T7351?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose 7017-T651 over 7017-T7351?
Pick 7017-T651 when strength drives the design, or when surface hardness matters. Pick 7017-T7351 when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 7017-T651 and 7017-T7351 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.