Aluminum 5052 vs 5A12
Aluminum · grade comparison
Aluminum 5052 and 5A12 are both aluminum grades. 5A12 is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 195 MPa (28.3 ksi) for 5052, about 8% more; tensile strength follows at 400 MPa (58 ksi) vs 230 MPa (33.4 ksi). 5A12 is the more ductile: elongation 18% versus 12% for 5052, and 5A12 is harder (95 HB vs 60 HB). 5052 runs hotter in service (150°C vs 65°C continuous) and 5052 conducts heat better (138 W/m·K vs 105 W/m·K). On the shop floor, 5052 welds better (excellent vs very good) and 5052 sits in a lower cost tier (budget, $) than 5A12 (premium, $$$).
5052Choose it when the part sees heat, or when it will be welded.
5A12Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
5052 vs 5A12: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Reduction in Area
Fracture Toughness (K_IC)
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Same in both: Machinability Rating (AISI 1212 = 100 %) 30%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 1,200 L/kg144 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 5052 | 5A12 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$$ Premium |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
5052 vs 5A12 — frequently asked
Is 5A12 stronger than 5052?
Yes. 5A12 has a typical yield strength of 210 MPa (30.5 ksi) against 195 MPa (28.3 ksi) for 5052 — about 8% more. Tensile strength is 400 MPa (58 ksi) vs 230 MPa (33.4 ksi).
Which is cheaper, 5052 or 5A12?
5052 is the lower-cost material: it sits in the budget tier ($) while 5A12 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 5052 or 5A12?
5052, by a small margin. Both rate fair for machinability — 50/100 against 42/100 for 5A12; for welding the order is 5052 first (excellent, 90/100) then 5A12 (very good, 72/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5052 and 5A12 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.