Aluminum 4015 vs 4032
Aluminum · grade comparison
Aluminum 4015 and 4032 are both aluminum grades. 4032 is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 55 MPa (7.98 ksi) for 4015, about 5.7 times as much; tensile strength follows at 380 MPa (55.1 ksi) vs 120 MPa (17.4 ksi). In exchange, 4015 is the more ductile: elongation 26% versus 9% for 4032, and 4032 is harder (120 HB vs 31 HB). 4032 is stiffer (79 GPa vs 70 GPa) and 4015 conducts heat better (165 W/m·K vs 141 W/m·K). On the shop floor, 4032 machines more easily (good vs poor), 4015 welds better (excellent vs fair), and 4032 sits in a lower cost tier (standard, $$) than 4015 (premium, $$$).
4015Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
4032Choose it when strength drives the design, or when the part is machined in volume.
4015 vs 4032: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 175°C347 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 12.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4015 | 4032 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| Anodizing Type II | — | Yes |
| Cerakote | — | Yes |
| Chem Film (Alodine) | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| Electropolishing | — | Yes |
| Hard Anodize Type III w/ PTFE | — | Yes |
| Hard Anodizing Type III | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Powder Coating | — | Yes |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
4015 vs 4032 — frequently asked
Is 4032 stronger than 4015?
Yes. 4032 has a typical yield strength of 315 MPa (45.7 ksi) against 55 MPa (7.98 ksi) for 4015 — about 5.7 times as much. Tensile strength is 380 MPa (55.1 ksi) vs 120 MPa (17.4 ksi).
Which is cheaper, 4015 or 4032?
4032 is the lower-cost material: it sits in the standard tier ($$) while 4015 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 4015 or 4032?
4032. Its machinability rates good (55/100) against poor (32/100) for 4015; for welding the order is 4015 first (excellent, 88/100) then 4032 (fair, 40/100).