Aluminum 3105-H14 vs 3105-O
Aluminum · 3105 temper comparison
3105-H14 and 3105-O are two conditions of the same aluminum grade, 3105: H14 (strain hardened, half hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. 3105-H14 is the stronger of the two: yield strength 150 MPa (21.8 ksi) against 55 MPa (7.98 ksi) for 3105-O, about 173% more; tensile strength follows at 170 MPa (24.7 ksi) vs 115 MPa (16.7 ksi). In exchange, 3105-O is the more ductile: elongation 24% versus 5% for 3105-H14, and 3105-H14 is harder (46 HB vs 28 HB). 3105-O runs hotter in service (200°C vs 150°C continuous). On the shop floor, 3105-H14 machines more easily (fair vs poor).
3105-H14Choose it when strength drives the design, or when the part is machined in volume.
3105-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
3105-H14 vs 3105-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.72 g/cm³0.1 lb/in³ · Melting Point (Solidus) 635°C1,175 °F · Liquidus Temperature 655°C1,211 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 897 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 4.2×10⁻⁸ Ω·m1.65 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 35% · Weldability 85 / 100 · Brazeability / Solderability 60 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
3105-H14 vs 3105-O — frequently asked
Is 3105-H14 stronger than 3105-O?
Yes. 3105-H14 has a typical yield strength of 150 MPa (21.8 ksi) against 55 MPa (7.98 ksi) for 3105-O — about 173% more. Tensile strength is 170 MPa (24.7 ksi) vs 115 MPa (16.7 ksi).
Which condition does FabDigit quote by default, H14 or O?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 3105-H14 or 3105-O?
3105-H14. Its machinability rates fair (44/100) against poor (30/100) for 3105-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 3105-H14 and 3105-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.