Aluminum 2014 vs AlSi7Mg
Aluminum · grade comparison
Aluminum 2014 and AlSi7Mg are both aluminum grades, both aerospace al. 2014 is the stronger of the two: yield strength 414 MPa (60 ksi) against 240 MPa (34.8 ksi) for AlSi7Mg, about 73% more; tensile strength follows at 483 MPa (70.1 ksi) vs 350 MPa (50.8 ksi). 2014 is the more ductile: elongation 13% versus 8% for AlSi7Mg, and 2014 is harder (135 HB vs 105 HB). AlSi7Mg is lighter (2.67 g/cm³ vs 2.8 g/cm³ for 2014) and 2014 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 2014 machines more easily (very good vs good) and AlSi7Mg welds better (very good vs poor).
2014Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AlSi7MgChoose it when weight is the constraint, or when it will be welded.
2014 vs AlSi7Mg: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Charpy V-Notch Impact (RT)
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2014 | AlSi7Mg |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| 3D printing | — | Yes |
| Default condition | — | As Printed |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodized (Aluminum AM) | — | Yes |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Plated (Metal AM) | — | Yes |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2014 vs AlSi7Mg — frequently asked
Is 2014 stronger than AlSi7Mg?
Yes. 2014 has a typical yield strength of 414 MPa (60 ksi) against 240 MPa (34.8 ksi) for AlSi7Mg — about 73% more. Tensile strength is 483 MPa (70.1 ksi) vs 350 MPa (50.8 ksi).
Which is cheaper, 2014 or AlSi7Mg?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 2014 or AlSi7Mg?
2014. Its machinability rates very good (78/100) against good (58/100) for AlSi7Mg; for welding the order is AlSi7Mg first (very good, 70/100) then 2014 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2014 and AlSi7Mg side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.