Aluminum 201.0-T4 vs 201.0-T7
Aluminum · 201.0 temper comparison
201.0-T4 and 201.0-T7 are two conditions of the same aluminum grade, 201.0: T4 (solution heat treated and naturally aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. 201.0-T7 is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 220 MPa (31.9 ksi) for 201.0-T4, about 91% more; tensile strength follows at 470 MPa (68.2 ksi) vs 380 MPa (55.1 ksi). In exchange, 201.0-T4 is the more ductile: elongation 18% versus 6% for 201.0-T7, and 201.0-T7 is harder (130 HB vs 95 HB). 201.0-T7 runs hotter in service (200°C vs 100°C continuous) and 201.0-T7 conducts electricity better (32 % IACS vs 28 % IACS).
201.0-T4Choose it when the part is bent, formed or impact-loaded.
201.0-T7Choose it when strength drives the design, or when the part sees heat.
201.0-T4 vs 201.0-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33 · Compressive Strength 425 MPa61.6 ksi
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 571°C1,060 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 920 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.3 µm/m·K10.7 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 70% · Weldability 25 / 100 · Formability (cold) 10 / 100 · Castability 35 / 100 · Brazeability / Solderability 20 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
201.0-T4 vs 201.0-T7 — frequently asked
Is 201.0-T7 stronger than 201.0-T4?
Yes. 201.0-T7 has a typical yield strength of 420 MPa (60.9 ksi) against 220 MPa (31.9 ksi) for 201.0-T4 — about 91% more. Tensile strength is 470 MPa (68.2 ksi) vs 380 MPa (55.1 ksi).
Which condition does FabDigit quote by default, T4 or T7?
T7 is the default 201.0 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 201.0-T4 or 201.0-T7?
201.0-T7, by a small margin. Both rate good for machinability — 65/100 against 58/100 for 201.0-T4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 201.0-T4 and 201.0-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.