Aluminum 1230A-H112 vs 1230A-H24
Aluminum · 1230A temper comparison
1230A-H112 and 1230A-H24 are two conditions of the same aluminum grade, 1230A: H112 (strain hardened from hot working only) versus H24 (strain hardened and partially annealed, half hard). The chemistry is identical, so every difference below comes from the condition. 1230A-H24 is the stronger of the two: yield strength 85 MPa (12.3 ksi) against 35 MPa (5.08 ksi) for 1230A-H112, about 143% more; tensile strength follows at 110 MPa (16 ksi) vs 85 MPa (12.3 ksi). In exchange, 1230A-H112 is the more ductile: elongation 25% versus 11% for 1230A-H24, and 1230A-H24 is harder (31 HB vs 24 HB). 1230A-H112 runs hotter in service (150°C vs 120°C continuous).
1230A-H112Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1230A-H24Choose it when strength drives the design.
1230A-H112 vs 1230A-H24: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 646°C1,195 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 72 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 75 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1230A-H112 vs 1230A-H24 — frequently asked
Is 1230A-H24 stronger than 1230A-H112?
Yes. 1230A-H24 has a typical yield strength of 85 MPa (12.3 ksi) against 35 MPa (5.08 ksi) for 1230A-H112 — about 143% more. Tensile strength is 110 MPa (16 ksi) vs 85 MPa (12.3 ksi).
Which condition does FabDigit quote by default, H112 or H24?
O is the default 1230A condition in the FabDigit quote flow (neither H112 nor H24). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1230A-H112 or 1230A-H24?
1230A-H24, by a small margin. Both rate poor for machinability — 32/100 against 27/100 for 1230A-H112.