Aluminum 1060-H112 vs 1060-O
Aluminum · 1060 temper comparison
1060-H112 and 1060-O are two conditions of the same aluminum grade, 1060: H112 (strain hardened from hot working only) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. 1060-H112 is the stronger of the two: yield strength 35 MPa (5.08 ksi) against 28 MPa (4.06 ksi) for 1060-O, about 25% more; tensile strength follows at 78 MPa (11.3 ksi) vs 70 MPa (10.2 ksi). In exchange, 1060-O is the more ductile: elongation 43% versus 25% for 1060-H112, and 1060-H112 is harder (21 HB vs 19 HB).
1060-H112Choose it when strength drives the design.
1060-OChoose it when the part is bent, formed or impact-loaded.
1060-H112 vs 1060-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 68 GPa9.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 646°C1,195 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 234 W/m·K135 BTU/hr·ft·°F · Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 62 % IACS · Electrical Resistivity 2.78×10⁻⁸ Ω·m1.09 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V · Corrosion Resistance 72 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 95 / 100 · Brazeability / Solderability 70 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1060-H112 vs 1060-O — frequently asked
Is 1060-H112 stronger than 1060-O?
Yes. 1060-H112 has a typical yield strength of 35 MPa (5.08 ksi) against 28 MPa (4.06 ksi) for 1060-O — about 25% more. Tensile strength is 78 MPa (11.3 ksi) vs 70 MPa (10.2 ksi).
Which condition does FabDigit quote by default, H112 or O?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 1060-H112 or 1060-O?
1060-H112, by a small margin. Both rate poor for machinability — 33/100 against 25/100 for 1060-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1060-H112 and 1060-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.