Aluminum 1050 vs 1080
Aluminum · grade comparison
Aluminum 1050 and 1080 are both aluminum grades. 1050 is the stronger of the two: yield strength 90 MPa (13.1 ksi) against 25 MPa (3.63 ksi) for 1080, about 3.6 times as much; tensile strength follows at 110 MPa (16 ksi) vs 70 MPa (10.2 ksi). In exchange, 1080 is the more ductile: elongation 43% versus 5% for 1050, and 1050 is harder (30 HB vs 20 HB).
1050Choose it when strength drives the design.
1080Choose it when the part is bent, formed or impact-loaded.
1050 vs 1080: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 646°C1,195 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -270°C-454 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 30%
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1050 | 1080 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.5 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
1050 vs 1080 — frequently asked
Is 1050 stronger than 1080?
Yes. 1050 has a typical yield strength of 90 MPa (13.1 ksi) against 25 MPa (3.63 ksi) for 1080 — about 3.6 times as much. Tensile strength is 110 MPa (16 ksi) vs 70 MPa (10.2 ksi).
Which is cheaper, 1050 or 1080?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose 1050 over 1080?
Pick 1050 when strength drives the design. Pick 1080 when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1050 and 1080 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.