Aluminum 1050-H111 vs 1050-H14
Aluminum · 1050 temper comparison
1050-H111 and 1050-H14 are two conditions of the same aluminum grade, 1050: H111 (slightly strain hardened) versus H14 (strain hardened, half hard). The chemistry is identical, so every difference below comes from the condition. 1050-H14 is the stronger of the two: yield strength 90 MPa (13.1 ksi) against 25 MPa (3.63 ksi) for 1050-H111, about 3.6 times as much; tensile strength follows at 110 MPa (16 ksi) vs 75 MPa (10.9 ksi). In exchange, 1050-H111 is the more ductile: elongation 30% versus 5% for 1050-H14, and 1050-H14 is harder (30 HB vs 20 HB). 1050-H111 runs hotter in service (200°C vs 150°C continuous).
1050-H111Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1050-H14Choose it when strength drives the design.
1050-H111 vs 1050-H14: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 646°C1,195 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -270°C-454 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1050-H111 vs 1050-H14 — frequently asked
Is 1050-H14 stronger than 1050-H111?
Yes. 1050-H14 has a typical yield strength of 90 MPa (13.1 ksi) against 25 MPa (3.63 ksi) for 1050-H111 — about 3.6 times as much. Tensile strength is 110 MPa (16 ksi) vs 75 MPa (10.9 ksi).
Which condition does FabDigit quote by default, H111 or H14?
H14 is the default 1050 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1050-H111 or 1050-H14?
1050-H14, by a small margin. Both rate poor for machinability — 30/100 against 24/100 for 1050-H111.