Cast Silicone TC
Additive grade
also RTV
TC = thermally conductive cast silicone
Alumina/boron-nitride filled potting or gap-pad grade for heat transfer with electrical insulation.
Values for the TC condition
Other Cast Silicone grades and fills
Cast Silicone is listed in 15 conditions; see the grade overview at Cast Silicone.
- FOAM
- Shore A 10
- TC
- Shore A 20
- ESD-COND
- Sn-cure
- Optical-clear
- Shore A 30
- FR-V0
- Shore A 40
- Pt-cure
- Shore A 50
- Shore A 60
- Shore A 70
- Shore A 80
Compare all 15 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Silicone foam | Blown low-density cast silicone for thermal/acoustic insulation and compliant compression seals. | — | 1 | 150 | 15 Shore A |
Ultra-soft cast silicone | Gel-like soft grade for skin-like effects, cushioning pads and delicate lifecasting. | — | 2 | 600 | 10 Shore A |
TCThis page Thermally conductive cast silicone | Alumina/boron-nitride filled potting or gap-pad grade for heat transfer with electrical insulation. | — | 3 | 120 | 55 Shore A |
Soft cast silicone | Soft, highly conformable grade for deep-undercut molds and soft-touch prototypes. | — | 3 | 550 | 20 Shore A |
Electrically conductive / ESD cast silicone | Carbon-black or silver-filled grade for EMI gaskets, contact pads and static-dissipative seals. | — | 4 | 150 | 60 Shore A |
Tin-cure (condensation-cure) cast silicone | Cheaper, inhibition-tolerant mold rubber; higher shrinkage, alcohol by-product and shorter shelf/mold life. | — | 4 | 380 | 35 Shore A |
Optically clear cast silicone | Water-clear unfilled/low-filler formulation for lenses, light guides, encapsulation and display parts. | — | 4 | 350 | 40 Shore A |
Soft mold-making grade | Most common mold-making hardness: easy demolding of detailed or undercut masters. | — | 4 | 450 | 30 Shore A |
Flame-retardant cast silicone | Filled/FR-additive formulation for electrical potting, rail and enclosure seals requiring V-0. | — | 5 | 250 | 50 Shore A |
Shore A 40Default General-purpose cast silicone | Balanced default: enough stiffness for stable mold walls and gaskets, still easily flexed. | — | 5 | 400 | 40 Shore A |
Platinum-cure (addition-cure) cast silicone | Pick for near-zero shrinkage, no cure by-products, long mold life and medical/food compliance; sensitive to sulfur/tin/latex inhibition. | — | 6 | 450 | 40 Shore A |
Medium-hard cast silicone | Choose for seals and pads needing better shape retention and lower deflection under load. | — | 7 | 350 | 11 Shore D |
Hard cast silicone | Stiffer grade for load-bearing gaskets, rollers, bushings and rigid mold shells. | — | 8 | 300 | 16 Shore D |
High-hardness cast silicone | Hardest common cast grade: dimensional stability and wear resistance where flexibility is secondary. | — | 9 | 250 | 22 Shore D |
Extra-hard cast silicone | Niche grade for stiff pads, wear strips and rigid inserts; low elongation, higher compression set. | — | 9 | 180 | 30 Shore D |
What is Cast Silicone TC?
Cast Silicone TC is Cast Silicone in the TC grade — alumina/boron-nitride filled potting or gap-pad grade for heat transfer with electrical insulation. Cast Silicone TC has a tensile strength of 3 MPa (0.435 ksi), weaker than 100% of silicone grades. Elongation at break is 120% and the elastic modulus is 0 GPa (5.8×10⁻⁴ Msi). Cast Silicone TC has a density of 2.2 g/cm³ (0.0795 lb/in³), heavier than 150% of silicone grades. Its glass-transition temperature is -122°C (-188 °F). Shore A 40 is the default condition FabDigit quotes; TC is available on request or by drawing note.
Advantages
- Conducts heat well — 1.5 W/m·K (0.867 BTU/hr·ft·°F), better than 150% of silicone grades
- Low, predictable mold shrinkage — 0.15%, better than 100% of silicone grades
Limitations
- Heavy — 2.2 g/cm³ (0.0795 lb/in³), worse than 150% of silicone grades
- Limited ductility — 120%, worse than 100% of silicone grades
- Limited formability — 70/100, worse than 100% of silicone grades
Cast Silicone TC properties
Typical room-temperature values for Cast Silicone TC; 16 are specific to this condition. Other listed values are Cast Silicone reference data and may not represent this condition. Bars are the position among silicone grades.
Physical5
Cast Silicone TC has a density of 2.2 g/cm³ (0.0795 lb/in³), heavier than 150% of silicone grades. Its glass-transition temperature is -122°C (-188 °F).
Mechanical7
Cast Silicone TC has a tensile strength of 3 MPa (0.435 ksi), weaker than 100% of silicone grades. Elongation at break is 120% and the elastic modulus is 0 GPa (5.8×10⁻⁴ Msi).
Thermal8
Cast Silicone TC is rated for continuous service to 200°C (392 °F). It conducts heat at 1.5 W/m·K (0.867 BTU/hr·ft·°F), better than 150% of silicone grades. Thermal expansion is 270 µm/m·K (150 µin/in·°F).
Electrical7
Cast Silicone TC is an electrical insulator with a dielectric strength of 15 kV/mm (381 V/mil) and a resistivity of 1×10¹² Ω·m.
Chemical & Environmental3
Corrosion resistance is excellent (85/100), better than 75% of silicone grades. UV resistance is excellent.
Sustainability4
Producing a kilogram of Cast Silicone TC takes about 130 MJ of energy and emits 7 kg of CO₂ — less than 100% of silicone grades. Typical recycled content is 0%.
Manufacturability5
Cast Silicone TC's machinability is poor (20/100, worse than 100% of silicone grades); formability very good (70/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Cast Silicone TC
Is Cast Silicone easy to machine?
Rarely machined; cured parts are best waterjet, laser or die cut, or frozen/backed before knife trimming — flash is removed by tumbling or trimming.
Can Cast Silicone be welded?
Not weldable; join by uncured silicone adhesive, self-bonding tape or platinum-cure over-molding onto a freshly cured, primed surface.
Can Cast Silicone be formed, bent or molded?
Two-part mix by weight, vacuum degas at ~29 inHg, pour in a thin stream to avoid entrapment; RT cure 4–24 h plus optional 1–4 h post-cure at 60–150 °C for full properties and low volatiles.
What surface finishes work on Cast Silicone?
Surface replicates the mold finish exactly; pigment in the mix rather than painting — paint only adheres via silicone-compatible primers, and plasma or primer treatment is needed for bonding.
Cast Silicone chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| silica filler (fumed / ground quartz)reinforcing and extending filler; sets hardness | 15 – 40 | 30 |
| SiH crosslinker (methylhydrogensiloxane)addition-cure systems | 0.5 – 5 | 2 |
| platinum catalyst (Karstedt)Pt-cure only; tin octoate in condensation systems | 5×10⁻⁴ – 0.01 | 0 |
| pigment / inhibitor / additives | 0 – 3 | 1 |
| polydimethylsiloxane (vinyl-terminated Pbase polymer | ≥ 55 (balance) | — |
Cast Silicone TC — frequently asked
What is Cast Silicone TC used for?
Cast Silicone TC is typically used for medical prototypes, seals and kitchenware. In short: platinum-cure silicone; high temp and biocompatible.
What is the tensile strength of Cast Silicone TC?
Cast Silicone TC has a typical tensile strength of 3 MPa (0.435 ksi) — weaker than 100% of silicone grades. Strength varies by condition: see the 15 listed tempers.
Is Cast Silicone TC easy to machine?
Not especially — machinability is rated poor (20/100, worse than 100% of silicone grades). Rarely machined; cured parts are best waterjet, laser or die cut, or frozen/backed before knife trimming — flash is removed by tumbling or trimming.
Can Cast Silicone TC be welded?
Not weldable; join by uncured silicone adhesive, self-bonding tape or platinum-cure over-molding onto a freshly cured, primed surface.
What surface finishes work on Cast Silicone TC?
Surface replicates the mold finish exactly; pigment in the mix rather than painting — paint only adheres via silicone-compatible primers, and plasma or primer treatment is needed for bonding.
Can Cast Silicone TC be formed, bent or molded?
Two-part mix by weight, vacuum degas at ~29 inHg, pour in a thin stream to avoid entrapment; RT cure 4–24 h plus optional 1–4 h post-cure at 60–150 °C for full properties and low volatiles.
What is the maximum service temperature of Cast Silicone TC?
Cast Silicone TC is rated for continuous use to about 200°C (392 °F), and briefly to 260°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in Cast Silicone TC?
Yes — Cast Silicone TC is available for urethane casting with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM D412 / D624 / D2240 / D395 — rubber tensile, tear, hardness, compression set — ASTM International (2022)
- Engineered Materials Handbook Vol. 2: Engineering Plastics / Elastomers — ASM International (1988)
- Mold Star & Dragon Skin platinum silicone technical bulletins — Smooth-On (2024)
- ELASTOSIL / SILPURAN RTV-2 silicone rubber datasheets — Wacker Chemie AG (2024)
- KE-series RTV silicone rubber product guide — Shin-Etsu Chemical (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.