MDF LDF (Light / ultralight MDF)
Grade
Choose for weight-critical or thick non-structural parts — display props, exhibition panels, model-making, lightweight case goods.
Values for the LDF condition
Other MDF tempers and conditions
MDF is listed in 4 conditions; see the grade overview at MDF.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
LDFThis page Light / ultralight MDF | Choose for weight-critical or thick non-structural parts — display props, exhibition panels, model-making, lightweight case goods. | — | 12 | — | — | 0.09 W/m·K |
Fire-retardant MDF | Specify where reaction-to-fire class B-s1,d0 / GB 8624 B1 is required — shopfitting, public interiors, wall linings. | — | 15 | — | — | 0.13 W/m·K |
moisture-resistant, MUF resin, green-tinted | Use in humid interior service — kitchen/bath cabinetry, worktop cores, laundry furniture; still not for exterior exposure. | — | 19 | — | — | 0.13 W/m·K |
High-density fibreboard | Pick when you need maximum stiffness, edge-profile crispness and screw holding — laminate flooring cores, thin door skins, speaker baffles. | — | 25 | — | — | 0.16 W/m·K |
What is MDF LDF?
MDF LDF is MDF in the LDF grade — choose for weight-critical or thick non-structural parts — display props, exhibition panels, model-making, lightweight case goods. MDF LDF has a tensile strength of 12 MPa (1.74 ksi), weaker than 68% of natural material grades. Elongation at break is 1% and the elastic modulus is 1.9 GPa (0.276 Msi). MDF LDF has a density of 0.6 g/cm³ (0.0217 lb/in³), lighter than 66% of natural material grades.
Advantages
- Easy to machine — 92/100, better than 97% of natural material grades
Limitations
- Needs corrosion protection — 15/100, worse than 100% of natural material grades
- Poor heat conductor — 0.09 W/m·K (0.052 BTU/hr·ft·°F), worse than 87% of natural material grades
- Low stiffness — 1.9 GPa (0.276 Msi), worse than 77% of natural material grades
- High embodied carbon — 0.85 kg CO₂/kg, worse than 76% of natural material grades
MDF LDF properties
Typical room-temperature values for MDF LDF; 12 are specific to this condition. Other listed values are MDF reference data and may not represent this condition. Bars are the position among natural material grades.
Physical2
MDF LDF has a density of 0.6 g/cm³ (0.0217 lb/in³), lighter than 66% of natural material grades.
Mechanical10
MDF LDF has a tensile strength of 12 MPa (1.74 ksi), weaker than 68% of natural material grades. Elongation at break is 1% and the elastic modulus is 1.9 GPa (0.276 Msi).
Thermal5
MDF LDF is rated for continuous service to 100°C (212 °F). It conducts heat at 0.09 W/m·K (0.052 BTU/hr·ft·°F), worse than 87% of natural material grades. Thermal expansion is 8 µm/m·K (4.44 µin/in·°F).
Electrical2
MDF LDF is an electrical insulator with a dielectric strength of 2.5 kV/mm (63.5 V/mil) and a resistivity of 1×10⁷ Ω·m.
Chemical & Environmental1
Corrosion resistance is poor (15/100), worse than 100% of natural material grades.
Sustainability4
Producing a kilogram of MDF LDF takes about 12 MJ of energy and emits 0.85 kg of CO₂ — more than 64% of natural material grades. Typical recycled content is 30%.
Manufacturability2
MDF LDF's machinability is excellent (92/100, better than 97% of natural material grades).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with MDF LDF
Is MDF easy to machine?
Machines like a soft isotropic solid — carbide or diamond-tipped router bits, high spindle speed and low feed give crisp profiles; the resin-laden dust is abrasive and respirable, so dust extraction and tool-life allowance are mandatory.
Can MDF be welded?
Not weldable; joints are made with PVA/PUR adhesive, dowels, confirmat screws or knock-down hardware, and screws into edges need pilot holes to avoid splitting.
Can MDF be formed, bent or molded?
Flat panels can be cold-formed only over large radii; use kerf-cutting, thin flexible MDF or postforming-grade panels for curves, and 3D-embossed doors are produced by membrane-press moulding of routed blanks.
What surface finishes work on MDF?
Faces take primer, UV lacquer, foil, melamine and veneer excellently; cut edges are porous and must be sealed with edge filler/PVA-primer or banded, and any water-based finish will raise the fibres unless the panel is sealed first.
MDF chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| urea-formaldehyde resinMUF/pMDI used for moisture-resistant and low-emission grades | 7 – 12 | 10 |
| paraffin wax emulsionhydrophobing agent | 0.4 – 1.5 | 0.9 |
| moistureequilibrium board moisture content as shipped | 4 – 9 | 6 |
| hardener / scavenger (ammonium salts, ur | 0.1 – 1 | 0.4 |
| fire-retardant salts (FR grade only)phosphate/borate loading in FR variant | 0 – 12 | 0 |
| wood fibre (cellulose/hemicellulose/lignrefined softwood/hardwood chips, sawmill residue and recovered wood | ≥ 78 (balance) | — |
MDF LDF — frequently asked
What is MDF LDF used for?
MDF LDF is typically used for furniture, cabinetry, moulding and trim, laminate flooring core and speaker enclosures. In short: best-machining wood panel; flattest paint-ready substrate; low-cost CNC-routed panel.
What is the tensile strength of MDF LDF?
MDF LDF has a typical tensile strength of 12 MPa (1.74 ksi) — weaker than 68% of natural material grades. Strength varies by condition: see the 4 listed tempers.
Is MDF LDF easy to machine?
Yes — machinability is rated excellent (92/100, better than 97% of natural material grades). Machines like a soft isotropic solid — carbide or diamond-tipped router bits, high spindle speed and low feed give crisp profiles; the resin-laden dust is abrasive and respirable, so dust extraction and tool-life allowance are mandatory.
Can MDF LDF be welded?
Not weldable; joints are made with PVA/PUR adhesive, dowels, confirmat screws or knock-down hardware, and screws into edges need pilot holes to avoid splitting.
What surface finishes work on MDF LDF?
Faces take primer, UV lacquer, foil, melamine and veneer excellently; cut edges are porous and must be sealed with edge filler/PVA-primer or banded, and any water-based finish will raise the fibres unless the panel is sealed first.
Can MDF LDF be formed, bent or molded?
Flat panels can be cold-formed only over large radii; use kerf-cutting, thin flexible MDF or postforming-grade panels for curves, and 3D-embossed doors are produced by membrane-press moulding of routed blanks.
What is the maximum service temperature of MDF LDF?
MDF LDF is rated for continuous use to about 100°C (212 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- EN 622-5 Fibreboards — Specifications, Part 5: Dry process boards (MDF) — CEN (2009)
- ANSI A208.2 Medium Density Fiberboard for Interior Applications — Composite Panel Association / ANSI (2016)
- ASTM D1037 Standard Test Methods for Evaluating Properties of Wood-Base Fiber and Particle Panel Materials — ASTM (2020)
- ASTM D1554 Standard Terminology Relating to Wood-Base Fiber and Particle Panel Materials — ASTM (2020)
- Wood Handbook — Wood as an Engineering Material, GTR-190, Ch. 11 Wood-Based Composite Materials — USDA Forest Products Laboratory (2010)
- Inventory of Carbon & Energy (ICE) v2 — timber & panel products — University of Bath / Circular Ecology (2011)
- Standard / MR / FR / ultralight MDF panel datasheets — Kronospan, Egger, Medite, Dare Global ( / ) (2024)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.