Magnesium Alloy EZ33A-F (As fabricated)
Temper
ASTM EZ33A · UNS M12330
Rarely supplied; only for non-critical parts or before final ageing, since EZ33A gains most of its stable strength from the T5 age.
Values for the F condition
Other EZ33A tempers and conditions
EZ33A is listed in 3 conditions; see the grade overview at EZ33A.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
FThis page As fabricated | Rarely supplied; only for non-critical parts or before final ageing, since EZ33A gains most of its stable strength from the T5 age. | 85 | 140 | 4 | 45 HB | 23 % IACS |
T5Default Cooled from hot working and artificially aged | Standard supply condition for aerospace sand castings: ~2–5 h at 215–220 °C gives stable properties and creep resistance to 250 °C. | 110 | 160 | 3 | 50 HB | 100 W/m·K |
T5 | Same ageing cycle applied to permanent-mould or investment castings; finer structure gives slightly higher strength and ductility than sand cast. | 110 | 170 | 4 | 52 HB | 24.6 % IACS |
What is EZ33A-F?
EZ33A-F is EZ33A in the F temper — rarely supplied; only for non-critical parts or before final ageing, since EZ33A gains most of its stable strength from the T5 age. EZ33A-F has a yield strength of 85 MPa (12.3 ksi) and a tensile strength of 140 MPa (20.3 ksi) — weaker than 97% of magnesium alloy grades. Elongation at break is 4% and the elastic modulus is 44 GPa (6.38 Msi). EZ33A-F has a density of 1.8 g/cm³ (0.065 lb/in³), lighter than 63% of magnesium alloy grades. It melts at 545°C (1,013 °F). T5 is the default condition FabDigit quotes; F is available on request or by drawing note.
Advantages
- Readily welded — 75/100, better than 91% of magnesium alloy grades
- High service temperature — 200°C (392 °F), better than 84% of magnesium alloy grades
Limitations
- Low strength — 85 MPa (12.3 ksi), worse than 97% of magnesium alloy grades
EZ33A-F properties
Typical room-temperature values for EZ33A-F; 20 are specific to this condition. Other listed values are EZ33A reference data and may not represent this condition. Bars are the position among magnesium alloy grades.
Physical3
EZ33A-F has a density of 1.8 g/cm³ (0.065 lb/in³), lighter than 63% of magnesium alloy grades. It melts at 545°C (1,013 °F).
Mechanical12
EZ33A-F has a yield strength of 85 MPa (12.3 ksi) and a tensile strength of 140 MPa (20.3 ksi) — weaker than 97% of magnesium alloy grades. Elongation at break is 4% and the elastic modulus is 44 GPa (6.38 Msi).
Thermal6
EZ33A-F is rated for continuous service to 200°C (392 °F). It conducts heat at 95 W/m·K (54.9 BTU/hr·ft·°F), worse than 52% of magnesium alloy grades. Thermal expansion is 26.1 µm/m·K (14.5 µin/in·°F).
Electrical3
EZ33A-F conducts electricity at 23 % IACS, better than 57% of magnesium alloy grades.
Chemical & Environmental3
Corrosion resistance is poor (28/100), better than 78% of magnesium alloy grades.
Sustainability4
Producing a kilogram of EZ33A-F takes about 350 MJ of energy and emits 30 kg of CO₂ — more than 74% of magnesium alloy grades. Typical recycled content is 10%.
Manufacturability8
EZ33A-F's machinability is excellent (95/100, better than 54% of magnesium alloy grades); weldability very good (75/100); formability not recommended (10/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with EZ33A-F
Is EZ33A easy to machine?
Machines extremely fast with sharp, high-rake tools and generous chip clearance; use dry or mineral-oil cutting (never water-based) and manage fine chips/dust as a fire hazard.
Can EZ33A be welded?
Readily GTAW-welded with matching EZ33A filler in argon; pre-clean thoroughly and re-age at ~215 °C after welding to restore local properties — commonly used for casting salvage.
Can EZ33A be formed, bent or molded?
Sand, permanent-mould and investment casting only; excellent fluidity and low microporosity give pressure-tight thin-wall parts, but SF6-free protective cover gas or flux and Zr grain refinement control are essential.
What surface finishes work on EZ33A?
Chromate/fluoride conversion coat or HAE/Dow 17/Tagnite anodic coating followed by epoxy primer and topcoat; isolate from steel and CFRP fasteners to avoid galvanic corrosion.
EZ33A chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Zn | 2 – 3.1 | 2.6 |
| RErare-earth (didymium/mischmetal, Ce-rich) | 2.5 – 4 | 3.2 |
| Zrgrain refiner | 0.5 – 1 | 0.7 |
| Cuimpurity limit | ≤ 0.1 | — |
| Niimpurity limit | ≤ 0.01 | — |
| Others (each)total 0.30 max | ≤ 0.1 | — |
| Mg | balance | — |
EZ33A-F — frequently asked
What is EZ33A-F used for?
EZ33A-F is typically used for aircraft engine casings, gearbox housings and pressure-tight castings for hydraulic components. In short: pressure-tight magnesium casting; stable to 250 °C; best weldability in family.
What is the yield strength of EZ33A-F?
EZ33A-F has a typical yield strength of 85 MPa (12.3 ksi) and a tensile strength of 140 MPa (20.3 ksi) — weaker than 97% of magnesium alloy grades. Strength varies by condition: see the 3 listed tempers.
Is EZ33A-F easy to machine?
Yes — machinability is rated excellent (95/100, better than 54% of magnesium alloy grades). Machines extremely fast with sharp, high-rake tools and generous chip clearance; use dry or mineral-oil cutting (never water-based) and manage fine chips/dust as a fire hazard.
Can EZ33A-F be welded?
Yes — weldability is rated very good (75/100). Readily GTAW-welded with matching EZ33A filler in argon; pre-clean thoroughly and re-age at ~215 °C after welding to restore local properties — commonly used for casting salvage.
What surface finishes work on EZ33A-F?
Chromate/fluoride conversion coat or HAE/Dow 17/Tagnite anodic coating followed by epoxy primer and topcoat; isolate from steel and CFRP fasteners to avoid galvanic corrosion.
Can EZ33A-F be formed, bent or molded?
Sand, permanent-mould and investment casting only; excellent fluidity and low microporosity give pressure-tight thin-wall parts, but SF6-free protective cover gas or flux and Zr grain refinement control are essential.
What is the maximum service temperature of EZ33A-F?
EZ33A-F is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between EZ33A-T5 and EZ33A-F?
T5 is the default condition — standard supply condition for aerospace sand castings: ~2–5 h at 215–220 °C gives stable properties and creep resistance to 250 °C. F: rarely supplied; only for non-critical parts or before final ageing, since EZ33A gains most of its stable strength from the T5 age. Yield strength is 110 MPa in T5 versus 85 MPa in F.
Sources
- ASTM B80 — Magnesium-Alloy Sand Castings — ASTM International (2015)
- AMS 4442 — Magnesium Alloy Castings, EZ33A-T5 — SAE International (2018)
- ASM Specialty Handbook: Magnesium and Magnesium Alloys — ASM International (1999)
- ASM Handbook Vol.2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol.13B — Corrosion: Materials — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.