Tungsten Alloy EWLa-1 vs WVMA (Doped Non-Sag Tungsten)
Tungsten Alloy · grade comparison
Tungsten Alloy EWLa-1 and WVMA (Doped Non-Sag Tungsten) are both tungsten alloy grades. WVMA (Doped Non-Sag Tungsten) is the stronger of the two: yield strength 1,900 MPa (276 ksi) against 850 MPa (123 ksi) for EWLa-1, about 124% more; tensile strength follows at 2,200 MPa (319 ksi) vs 1,100 MPa (160 ksi). WVMA (Doped Non-Sag Tungsten) is the more ductile: elongation 2.5% versus 2% for EWLa-1. WVMA (Doped Non-Sag Tungsten) runs hotter in service (2,000°C vs 400°C continuous).
WVMA (Doped Non-Sag Tungsten)Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
EWLa-1 vs WVMA (Doped Non-Sag Tungsten): propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
EWLa-1WVMA (Doped Non-Sag Tungsten)
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 400 GPa58 Msi · Bulk Modulus 310 GPa45 Msi · Poisson's Ratio 0.28 · Charpy V-Notch Impact (RT) 2 J1.5 ft·lbf · Hardness, Brinell 455 HB · Hardness, Vickers 480 HV
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 3,422°C6,192 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 4.5 µm/m·K2.5 µin/in·°F · Latent Heat of Fusion 192 J/g82.5 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Energy (primary production) 380 MJ/kg163,371 BTU/lb · Embodied Water 300 L/kg35.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every tungsten alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | EWLa-1 | WVMA (Doped Non-Sag Tungsten) |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
EWLa-1 vs WVMA (Doped Non-Sag Tungsten) — frequently asked
Is WVMA (Doped Non-Sag Tungsten) stronger than EWLa-1?
Yes. WVMA (Doped Non-Sag Tungsten) has a typical yield strength of 1,900 MPa (276 ksi) against 850 MPa (123 ksi) for EWLa-1 — about 124% more. Tensile strength is 2,200 MPa (319 ksi) vs 1,100 MPa (160 ksi).
Which is cheaper, EWLa-1 or WVMA (Doped Non-Sag Tungsten)?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, EWLa-1 or WVMA (Doped Non-Sag Tungsten)?
WVMA (Doped Non-Sag Tungsten). Its weldability rates poor (15/100) against not recommended (10/100) for EWLa-1.
Ready to make it?
Upload a CAD file and FabDigit prices the part in EWLa-1 and WVMA (Doped Non-Sag Tungsten) side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.