Titanium Ti-13V-11Cr-3Al-CWA vs Ti-13V-11Cr-3Al-STA
Titanium · Ti-13V-11Cr-3Al temper comparison
Ti-13V-11Cr-3Al-CWA and Ti-13V-11Cr-3Al-STA are two conditions of the same titanium grade, Ti-13V-11Cr-3Al: CWA (cold worked and aged) versus STA (solution treated and aged). The chemistry is identical, so every difference below comes from the condition. Ti-13V-11Cr-3Al-CWA is the stronger of the two: yield strength 1,330 MPa (193 ksi) against 1,170 MPa (170 ksi) for Ti-13V-11Cr-3Al-STA, about 14% more; tensile strength follows at 1,400 MPa (203 ksi) vs 1,220 MPa (177 ksi). In exchange, Ti-13V-11Cr-3Al-STA is the more ductile: elongation 8% versus 4% for Ti-13V-11Cr-3Al-CWA, and Ti-13V-11Cr-3Al-STA is harder (380 HB vs 300 HB).
Ti-13V-11Cr-3Al-CWAChoose it when strength drives the design.
Ti-13V-11Cr-3Al-STAChoose it when the part is bent, formed or impact-loaded.
Ti-13V-11Cr-3Al-CWA vs Ti-13V-11Cr-3Al-STA: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Ti-13V-11Cr-3Al-CWATi-13V-11Cr-3Al-STA
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 40 GPa5.8 Msi · Bulk Modulus 95 GPa13.8 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Same in both: Density 4.87 g/cm³0.18 lb/in³ · Melting Point (Solidus) 1,427°C2,601 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 7.8 W/m·K4.5 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9 µm/m·K5 µin/in·°F · Latent Heat of Fusion 320 J/g138 BTU/lb · Max Service Temperature (continuous) 315°C599 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.2 % IACS · Electrical Resistivity 1.4×10⁻⁶ Ω·m55.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V · Corrosion Resistance 88 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 45 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ti-13V-11Cr-3Al-CWA vs Ti-13V-11Cr-3Al-STA — frequently asked
Is Ti-13V-11Cr-3Al-CWA stronger than Ti-13V-11Cr-3Al-STA?
Yes. Ti-13V-11Cr-3Al-CWA has a typical yield strength of 1,330 MPa (193 ksi) against 1,170 MPa (170 ksi) for Ti-13V-11Cr-3Al-STA — about 14% more. Tensile strength is 1,400 MPa (203 ksi) vs 1,220 MPa (177 ksi).
Which condition does FabDigit quote by default, CWA or STA?
ST is the default Ti-13V-11Cr-3Al condition in the FabDigit quote flow (neither CWA nor STA). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Ti-13V-11Cr-3Al-CWA or Ti-13V-11Cr-3Al-STA?
Ti-13V-11Cr-3Al-STA. Its weldability rates poor (30/100) against poor (25/100) for Ti-13V-11Cr-3Al-CWA.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti-13V-11Cr-3Al-CWA and Ti-13V-11Cr-3Al-STA side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.