Titanium Grade Ti-Pd7B-AW vs Grade Ti-Pd7B-F
Titanium · Grade Ti-Pd7B temper comparison
Grade Ti-Pd7B-AW and Grade Ti-Pd7B-F are two conditions of the same titanium grade, Grade Ti-Pd7B: AW (as-welded deposit) versus F (as fabricated). The chemistry is identical, so every difference below comes from the condition. Grade Ti-Pd7B-AW is the stronger of the two: yield strength 400 MPa (58 ksi) against 375 MPa (54.4 ksi) for Grade Ti-Pd7B-F, about 7% more; tensile strength follows at 470 MPa (68.2 ksi) vs 445 MPa (64.5 ksi). In exchange, Grade Ti-Pd7B-F is the more ductile: elongation 16% versus 14% for Grade Ti-Pd7B-AW, and Grade Ti-Pd7B-AW is harder (165 HB vs 152 HB).
Grade Ti-Pd7B-AWChoose it when strength drives the design.
Grade Ti-Pd7B-FChoose it when the part is bent, formed or impact-loaded.
Grade Ti-Pd7B-AW vs Grade Ti-Pd7B-F: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Grade Ti-Pd7B-AWGrade Ti-Pd7B-F
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 365 J/g157 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.08 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Castability 62 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 750 MJ/kg322,442 BTU/lb · Embodied Carbon (primary production) 46 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Grade Ti-Pd7B-AW vs Grade Ti-Pd7B-F — frequently asked
Is Grade Ti-Pd7B-AW stronger than Grade Ti-Pd7B-F?
Yes. Grade Ti-Pd7B-AW has a typical yield strength of 400 MPa (58 ksi) against 375 MPa (54.4 ksi) for Grade Ti-Pd7B-F — about 7% more. Tensile strength is 470 MPa (68.2 ksi) vs 445 MPa (64.5 ksi).
Which condition does FabDigit quote by default, AW or F?
A is the default Grade Ti-Pd7B condition in the FabDigit quote flow (neither AW nor F). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Grade Ti-Pd7B-AW or Grade Ti-Pd7B-F?
Grade Ti-Pd7B-F. Its weldability rates excellent (85/100) against very good (80/100) for Grade Ti-Pd7B-AW.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade Ti-Pd7B-AW and Grade Ti-Pd7B-F side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.