Titanium Grade 2 vs Ti-4Al-4Mo-2Sn
Titanium · grade comparison
Titanium Grade 2 and Ti-4Al-4Mo-2Sn are both titanium grades. Ti-4Al-4Mo-2Sn is the stronger of the two: yield strength 1,030 MPa (149 ksi) against 380 MPa (55.1 ksi) for Grade 2, about 171% more; tensile strength follows at 1,150 MPa (167 ksi) vs 440 MPa (63.8 ksi). In exchange, Grade 2 is the more ductile: elongation 28% versus 13% for Ti-4Al-4Mo-2Sn, and Ti-4Al-4Mo-2Sn is harder (332 HB vs 150 HB). Ti-4Al-4Mo-2Sn is stiffer (114 GPa vs 103 GPa) and Ti-4Al-4Mo-2Sn runs hotter in service (425°C vs 300°C continuous). On the shop floor, Grade 2 machines more easily (fair vs poor), Grade 2 welds better (excellent vs poor), and Ti-4Al-4Mo-2Sn sits in a lower cost tier (high, $$$$) than Grade 2 (specialty, $$$$$).
Grade 2Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
Ti-4Al-4Mo-2SnChoose it when strength drives the design, or when the part sees heat.
Grade 2 vs Ti-4Al-4Mo-2Sn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 365 J/g157 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Brazeability / Solderability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 8
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 2 | Ti-4Al-4Mo-2Sn |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 2 vs Ti-4Al-4Mo-2Sn — frequently asked
Is Ti-4Al-4Mo-2Sn stronger than Grade 2?
Yes. Ti-4Al-4Mo-2Sn has a typical yield strength of 1,030 MPa (149 ksi) against 380 MPa (55.1 ksi) for Grade 2 — about 171% more. Tensile strength is 1,150 MPa (167 ksi) vs 440 MPa (63.8 ksi).
Which is cheaper, Grade 2 or Ti-4Al-4Mo-2Sn?
Ti-4Al-4Mo-2Sn is the lower-cost material: it sits in the high tier ($$$$) while Grade 2 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Grade 2 or Ti-4Al-4Mo-2Sn?
Grade 2. Its machinability rates fair (40/100) against poor (16/100) for Ti-4Al-4Mo-2Sn; for welding the order is Grade 2 first (excellent, 90/100) then Ti-4Al-4Mo-2Sn (poor, 28/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 2 and Ti-4Al-4Mo-2Sn side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.