Titanium ERTi-9-ANN vs ERTi-9-AW
Titanium · ERTi-9 temper comparison
ERTi-9-ANN and ERTi-9-AW are two conditions of the same titanium grade, ERTi-9: ANN (annealed) versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. ERTi-9-AW is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 550 MPa (79.8 ksi) for ERTi-9-ANN, about 6% more. In exchange, ERTi-9-ANN is the more ductile: elongation 20% versus 15% for ERTi-9-AW, and ERTi-9-AW is harder (265 HV vs 250 HV).
ERTi-9-ANNChoose it when the part is bent, formed or impact-loaded.
ERTi-9-AWChoose it when strength drives the design.
ERTi-9-ANN vs ERTi-9-AW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.32 · Shear Strength 450 MPa65.3 ksi · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in · Charpy V-Notch Impact (RT) 22 J16.2 ft·lbf · Hardness, Rockwell B 100 HRB
Physical
Density and transition temperatures.
Same in both: Density 4.48 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,650°C3,002 °F · Liquidus Temperature 1,700°C3,092 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 7.6 W/m·K4.4 BTU/hr·ft·°F · Specific Heat Capacity 544 J/kg·K0.13 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.4 µm/m·K5.2 µin/in·°F · Latent Heat of Fusion 295 J/g127 BTU/lb · Max Service Temperature (continuous) 315°C599 °F · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.4 % IACS · Electrical Resistivity 1.26×10⁻⁶ Ω·m49.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 88 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Same in both: Machinability 25 / 100 · Machinability Rating (AISI 1212 = 100 %) 22% · Weldability 90 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ERTi-9-ANN vs ERTi-9-AW — frequently asked
Is ERTi-9-AW stronger than ERTi-9-ANN?
Yes. ERTi-9-AW has a typical yield strength of 585 MPa (84.8 ksi) against 550 MPa (79.8 ksi) for ERTi-9-ANN — about 6% more. Tensile strength is 690 MPa (100 ksi) vs 660 MPa (95.7 ksi).
Which condition does FabDigit quote by default, ANN or AW?
AW is the default ERTi-9 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ERTi-9-ANN over ERTi-9-AW?
Pick ERTi-9-ANN when the part is bent, formed or impact-loaded. Pick ERTi-9-AW when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ERTi-9-ANN and ERTi-9-AW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.