Steel ZG65Mn-N vs ZG65Mn QT-48-52HRC
Steel · ZG65Mn temper comparison
ZG65Mn-N and ZG65Mn QT-48-52HRC are two conditions of the same steel grade, ZG65Mn: N (normalized) versus QT-48-52HRC. The chemistry is identical, so every difference below comes from the condition. ZG65Mn QT-48-52HRC is the stronger of the two: yield strength 1,300 MPa (189 ksi) against 580 MPa (84.1 ksi) for ZG65Mn-N, about 124% more; tensile strength follows at 1,600 MPa (232 ksi) vs 930 MPa (135 ksi). In exchange, ZG65Mn-N is the more ductile: elongation 7% versus 2% for ZG65Mn QT-48-52HRC, and ZG65Mn-N is harder (275 HB vs 250 HB). ZG65Mn-N runs hotter in service (300°C vs 200°C continuous). On the shop floor, ZG65Mn-N machines more easily (poor vs not recommended) and ZG65Mn-N welds better (poor vs not recommended).
ZG65Mn-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
ZG65Mn QT-48-52HRCChoose it when strength drives the design.
ZG65Mn-N vs ZG65Mn QT-48-52HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 62 / 100 · Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZG65Mn-N vs ZG65Mn QT-48-52HRC — frequently asked
Is ZG65Mn QT-48-52HRC stronger than ZG65Mn-N?
Yes. ZG65Mn QT-48-52HRC has a typical yield strength of 1,300 MPa (189 ksi) against 580 MPa (84.1 ksi) for ZG65Mn-N — about 124% more. Tensile strength is 1,600 MPa (232 ksi) vs 930 MPa (135 ksi).
Which condition does FabDigit quote by default, N or QT-48-52HRC?
N+T is the default ZG65Mn condition in the FabDigit quote flow (neither N nor QT-48-52HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, ZG65Mn-N or ZG65Mn QT-48-52HRC?
ZG65Mn-N. Its machinability rates poor (34/100) against not recommended (12/100) for ZG65Mn QT-48-52HRC; for welding the order is ZG65Mn-N first (poor, 20/100) then ZG65Mn QT-48-52HRC (not recommended, 8/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZG65Mn-N and ZG65Mn QT-48-52HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.