Steel WC6 N+T vs WC6 Q+T
Steel · WC6 temper comparison
WC6 N+T and WC6 Q+T are two conditions of the same steel grade, WC6: N+T (normalized and tempered) versus Q+T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. WC6 Q+T is the stronger of the two: yield strength 400 MPa (58 ksi) against 340 MPa (49.3 ksi) for WC6 N+T, about 18% more; tensile strength follows at 585 MPa (84.8 ksi) vs 530 MPa (76.9 ksi). WC6 Q+T is harder — 190 HB against 170 HB for WC6 N+T — which matters for wear surfaces and threads.
WC6 Q+TChoose it when strength drives the design, or when surface hardness matters.
WC6 N+T vs WC6 Q+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 345 MPa50 ksi · Shear Strength 330 MPa47.9 ksi · Fracture Toughness (K_IC) 130 MPa·√m118 ksi·√in · Hardness, Rockwell B 87 HRB · Hardness, Vickers 180 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 470°C878 °F · Min Service Temperature -29°C-20 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 16 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 65 / 100 · Formability (cold) 20 / 100 · Castability 75 / 100 · Brazeability / Solderability 55 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 27 MJ/kg11,608 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
WC6 N+T vs WC6 Q+T — frequently asked
Is WC6 Q+T stronger than WC6 N+T?
Yes. WC6 Q+T has a typical yield strength of 400 MPa (58 ksi) against 340 MPa (49.3 ksi) for WC6 N+T — about 18% more. Tensile strength is 585 MPa (84.8 ksi) vs 530 MPa (76.9 ksi).
Which condition does FabDigit quote by default, N+T or Q+T?
N+T is the default WC6 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, WC6 N+T or WC6 Q+T?
WC6 N+T. Its machinability rates good (55/100) against fair (50/100) for WC6 Q+T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in WC6 N+T and WC6 Q+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.