Steel SCr435-A vs SCr435 QT 25-30 HRC
Steel · SCr435 temper comparison
SCr435-A and SCr435 QT 25-30 HRC are two conditions of the same steel grade, SCr435: A (solution annealed) versus QT 25-30 HRC. The chemistry is identical, so every difference below comes from the condition. SCr435 QT 25-30 HRC is the stronger of the two: yield strength 750 MPa (109 ksi) against 350 MPa (50.8 ksi) for SCr435-A, about 114% more; tensile strength follows at 900 MPa (131 ksi) vs 600 MPa (87 ksi). In exchange, SCr435-A is the more ductile: elongation 25% versus 19% for SCr435 QT 25-30 HRC, and SCr435 QT 25-30 HRC is harder (265 HB vs 197 HB).
SCr435-AChoose it when the part is bent, formed or impact-loaded.
SCr435 QT 25-30 HRCChoose it when strength drives the design.
SCr435-A vs SCr435 QT 25-30 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SCr435-A vs SCr435 QT 25-30 HRC — frequently asked
Is SCr435 QT 25-30 HRC stronger than SCr435-A?
Yes. SCr435 QT 25-30 HRC has a typical yield strength of 750 MPa (109 ksi) against 350 MPa (50.8 ksi) for SCr435-A — about 114% more. Tensile strength is 900 MPa (131 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, A or QT 25-30 HRC?
QT is the default SCr435 condition in the FabDigit quote flow (neither A nor QT 25-30 HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SCr435-A or SCr435 QT 25-30 HRC?
SCr435-A. Its machinability rates good (60/100) against fair (54/100) for SCr435 QT 25-30 HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SCr435-A and SCr435 QT 25-30 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.