Steel P265GH Annealed vs P265GH Q&T
Steel · P265GH temper comparison
P265GH Annealed and P265GH Q&T are two conditions of the same steel grade, P265GH: Annealed versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. P265GH Q&T is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 275 MPa (39.9 ksi) for P265GH Annealed, about 24% more; tensile strength follows at 500 MPa (72.5 ksi) vs 430 MPa (62.4 ksi). In exchange, P265GH Annealed is the more ductile: elongation 32% versus 26% for P265GH Q&T, and P265GH Q&T is harder (150 HB vs 120 HB).
P265GH AnnealedChoose it when the part is bent, formed or impact-loaded.
P265GH Q&TChoose it when strength drives the design.
P265GH Annealed vs P265GH Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 211 GPa30.6 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 60%
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 461 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -10°C14 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 10 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 70 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
P265GH Annealed vs P265GH Q&T — frequently asked
Is P265GH Q&T stronger than P265GH Annealed?
Yes. P265GH Q&T has a typical yield strength of 340 MPa (49.3 ksi) against 275 MPa (39.9 ksi) for P265GH Annealed — about 24% more. Tensile strength is 500 MPa (72.5 ksi) vs 430 MPa (62.4 ksi).
Which condition does FabDigit quote by default, Annealed or Q&T?
HR is the default P265GH condition in the FabDigit quote flow (neither Annealed nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, P265GH Annealed or P265GH Q&T?
P265GH Annealed. Its machinability rates very good (72/100) against good (63/100) for P265GH Q&T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in P265GH Annealed and P265GH Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.