Steel Hardox 600 vs S890Q
Steel · grade comparison
Steel Hardox 600 and S890Q are both steel grades. Hardox 600 is the stronger of the two: yield strength 1,650 MPa (239 ksi) against 930 MPa (135 ksi) for S890Q, about 77% more; tensile strength follows at 2,000 MPa (290 ksi) vs 1,000 MPa (145 ksi). In exchange, S890Q is the more ductile: elongation 13% versus 7% for Hardox 600, and Hardox 600 is harder (600 HB vs 310 HB). S890Q runs hotter in service (350°C vs 250°C continuous) and S890Q conducts heat better (35 W/m·K vs 30 W/m·K). On the shop floor, S890Q machines more easily (fair vs not recommended), S890Q welds better (good vs poor), and S890Q sits in a lower cost tier (budget, $) than Hardox 600 (standard, $$).
Hardox 600Choose it when strength drives the design.
S890QChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Hardox 600 vs S890Q: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Hardox 600 | S890Q |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
Hardox 600 vs S890Q — frequently asked
Is Hardox 600 stronger than S890Q?
Yes. Hardox 600 has a typical yield strength of 1,650 MPa (239 ksi) against 930 MPa (135 ksi) for S890Q — about 77% more. Tensile strength is 2,000 MPa (290 ksi) vs 1,000 MPa (145 ksi).
Which is cheaper, Hardox 600 or S890Q?
S890Q is the lower-cost material: it sits in the budget tier ($) while Hardox 600 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Hardox 600 or S890Q?
S890Q. Its machinability rates fair (35/100) against not recommended (8/100) for Hardox 600; for welding the order is S890Q first (good, 55/100) then Hardox 600 (poor, 30/100).