Steel A517 Grade B vs Hardox 600
Steel · grade comparison
Steel A517 Grade B and Hardox 600 are both steel grades. Hardox 600 is the stronger of the two: yield strength 1,650 MPa (239 ksi) against 760 MPa (110 ksi) for A517 Grade B, about 117% more; tensile strength follows at 2,000 MPa (290 ksi) vs 860 MPa (125 ksi). In exchange, A517 Grade B is the more ductile: elongation 18% versus 7% for Hardox 600, and Hardox 600 is harder (600 HB vs 255 HB). A517 Grade B runs hotter in service (370°C vs 250°C continuous) and A517 Grade B conducts heat better (42 W/m·K vs 30 W/m·K). On the shop floor, A517 Grade B machines more easily (fair vs not recommended), A517 Grade B welds better (good vs poor), and A517 Grade B sits in a lower cost tier (budget, $) than Hardox 600 (standard, $$).
A517 Grade BChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Hardox 600Choose it when strength drives the design.
A517 Grade B vs Hardox 600: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A517 Grade B | Hardox 600 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A517 Grade B vs Hardox 600 — frequently asked
Is Hardox 600 stronger than A517 Grade B?
Yes. Hardox 600 has a typical yield strength of 1,650 MPa (239 ksi) against 760 MPa (110 ksi) for A517 Grade B — about 117% more. Tensile strength is 2,000 MPa (290 ksi) vs 860 MPa (125 ksi).
Which is cheaper, A517 Grade B or Hardox 600?
A517 Grade B is the lower-cost material: it sits in the budget tier ($) while Hardox 600 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A517 Grade B or Hardox 600?
A517 Grade B. Its machinability rates fair (38/100) against not recommended (8/100) for Hardox 600; for welding the order is A517 Grade B first (good, 55/100) then Hardox 600 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A517 Grade B and Hardox 600 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.