Steel H41-HR vs H41-HT52
Steel · H41 temper comparison
H41-HR and H41-HT52 are two conditions of the same steel grade, H41: HR (hot rolled) versus HT52 (hardened and tempered). The chemistry is identical, so every difference below comes from the condition. H41-HT52 is the stronger of the two: yield strength 1,450 MPa (210 ksi) against 760 MPa (110 ksi) for H41-HR, about 91% more; tensile strength follows at 1,750 MPa (254 ksi) vs 1,010 MPa (146 ksi). In exchange, H41-HR is the more ductile: elongation 11% versus 7% for H41-HT52, and H41-HR is harder (300 HB vs 217 HB). H41-HT52 runs hotter in service (600°C vs 400°C continuous). On the shop floor, H41-HT52 welds better (25 vs 15 out of 100).
H41-HRChoose it when the part is bent, formed or impact-loaded.
H41-HT52Choose it when strength drives the design, or when the part sees heat.
H41-HR vs H41-HT52: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Hardness, Rockwell B 96 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.88 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.7 % IACS · Electrical Resistivity 6.4×10⁻⁷ Ω·m25.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 14 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 35 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 42 MJ/kg18,057 BTU/lb · Embodied Carbon (primary production) 3.1 kg CO₂/kg · Embodied Water 85 L/kg10.2 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
H41-HR vs H41-HT52 — frequently asked
Is H41-HT52 stronger than H41-HR?
Yes. H41-HT52 has a typical yield strength of 1,450 MPa (210 ksi) against 760 MPa (110 ksi) for H41-HR — about 91% more. Tensile strength is 1,750 MPa (254 ksi) vs 1,010 MPa (146 ksi).
Which condition does FabDigit quote by default, HR or HT52?
ANN is the default H41 condition in the FabDigit quote flow (neither HR nor HT52). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, H41-HR or H41-HT52?
H41-HR, by a small margin. Both rate poor for machinability — 25/100 against 16/100 for H41-HT52; for welding the order is H41-HT52 first (poor, 25/100) then H41-HR (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in H41-HR and H41-HT52 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.