Steel E80C-B2 vs ER70S-3
Steel · grade comparison
Steel E80C-B2 and ER70S-3 are both steel grades. E80C-B2 is the stronger of the two: yield strength 505 MPa (73.2 ksi) against 460 MPa (66.7 ksi) for ER70S-3, about 10% more; tensile strength follows at 600 MPa (87 ksi) vs 550 MPa (79.8 ksi). In exchange, ER70S-3 is the more ductile: elongation 28% versus 23% for E80C-B2, and E80C-B2 is harder (190 HB vs 160 HB). E80C-B2 runs hotter in service (550°C vs 400°C continuous) and ER70S-3 conducts heat better (48 W/m·K vs 40 W/m·K). On the shop floor, ER70S-3 welds better (excellent vs very good) and ER70S-3 sits in a lower cost tier (budget, $) than E80C-B2 (premium, $$$).
E80C-B2Choose it when strength drives the design, or when the part sees heat.
ER70S-3Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
E80C-B2 vs ER70S-3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Formability (cold)
Castability
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E80C-B2 | ER70S-3 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
E80C-B2 vs ER70S-3 — frequently asked
Is E80C-B2 stronger than ER70S-3?
Yes. E80C-B2 has a typical yield strength of 505 MPa (73.2 ksi) against 460 MPa (66.7 ksi) for ER70S-3 — about 10% more. Tensile strength is 600 MPa (87 ksi) vs 550 MPa (79.8 ksi).
Which is cheaper, E80C-B2 or ER70S-3?
ER70S-3 is the lower-cost material: it sits in the budget tier ($) while E80C-B2 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, E80C-B2 or ER70S-3?
ER70S-3. Its weldability rates excellent (95/100) against very good (75/100) for E80C-B2.